Constellium Planoxal® 60 Aluminum plate

Category Metal , Nonferrous Metal , Aluminum Alloy , 6000 Series Aluminum Alloy
Manufacturer Constellium
Trade Name Planoxal®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Constellium Planoxal® 60 Aluminum plate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
The advantage of Planoxal®-60 plates over other standard EN AW-6082 alloy products is their low level of internal stress. They are also suitable for technical anodizing. Planoxal®-60 is mainly used for medium stressed machine elements which are subject to heavy machining, particularly for parts that require anodizing. Applications include packaging, printing and handling machines.Information provided by manufacturer
Physical Properties Metric English Comments
Density 2.70 g/cc
0.0975 lb/in³
Mechanical Properties Metric English Comments
Hardness, Brinell 105

@Thickness 4.99 - 20.0 mm
105

@Thickness 0.196 - 0.787 in
105

@Thickness 20.0 - 80.0 mm
105

@Thickness 0.787 - 3.15 in
Tensile Strength >= 295 MPa

@Thickness 12.5 - 60.0 mm
>= 42800 psi

@Thickness 0.492 - 2.36 in
Temper T651; Standard EN 485-2
>= 295 MPa

@Thickness 60.0 - 80.0 mm
>= 42800 psi

@Thickness 2.36 - 3.15 in
Temper T651; Standard EN 485-2
>= 300 MPa

@Thickness 6.00 - 12.0 mm
>= 43500 psi

@Thickness 0.236 - 0.472 in
Temper T651; Standard EN 485-2
>= 310 MPa

@Thickness 4.99 - 6.00 mm
>= 45000 psi

@Thickness 0.196 - 0.236 in
Temper T651; Standard EN 485-2
350 MPa

@Thickness 4.99 - 20.0 mm
50800 psi

@Thickness 0.196 - 0.787 in
Typical Strength
350 MPa

@Thickness 20.0 - 80.0 mm
50800 psi

@Thickness 0.787 - 3.15 in
Typical Strength
Tensile Strength, Yield >= 240 MPa

@Strain 0.200 %,
Thickness 12.5 - 60.0 mm
>= 34800 psi

@Strain 0.200 %,
Thickness 0.492 - 2.36 in
Temper T651; Standard EN 485-2
>= 240 MPa

@Strain 0.200 %,
Thickness 60.0 - 80.0 mm
>= 34800 psi

@Strain 0.200 %,
Thickness 2.36 - 3.15 in
Temper T651; Standard EN 485-2
>= 255 MPa

@Strain 0.200 %,
Thickness 6.00 - 12.0 mm
>= 37000 psi

@Strain 0.200 %,
Thickness 0.236 - 0.472 in
Temper T651; Standard EN 485-2
>= 260 MPa

@Strain 0.200 %,
Thickness 4.99 - 6.00 mm
>= 37700 psi

@Strain 0.200 %,
Thickness 0.196 - 0.236 in
Temper T651; Standard EN 485-2
305 MPa

@Strain 0.200 %,
Thickness 4.99 - 20.0 mm
44200 psi

@Strain 0.200 %,
Thickness 0.196 - 0.787 in
Typical Strength
310 MPa

@Strain 0.200 %,
Thickness 20.0 - 80.0 mm
45000 psi

@Strain 0.200 %,
Thickness 0.787 - 3.15 in
Typical Strength
Elongation at Break >= 7.0 %

@Thickness 60.0 - 80.0 mm
>= 7.0 %

@Thickness 2.36 - 3.15 in
Temper T651; Standard EN 485-2
>= 8.0 %

@Thickness 12.5 - 60.0 mm
>= 8.0 %

@Thickness 0.492 - 2.36 in
Temper T651; Standard EN 485-2
>= 9.0 %

@Thickness 6.00 - 12.0 mm
>= 9.0 %

@Thickness 0.236 - 0.472 in
Temper T651; Standard EN 485-2
>= 10 %

@Thickness 4.99 - 6.00 mm
>= 10 %

@Thickness 0.196 - 0.236 in
Temper T651; Standard EN 485-2
11 %

@Thickness 4.99 - 20.0 mm
11 %

@Thickness 0.196 - 0.787 in
Typical Elongation
11 %

@Thickness 20.0 - 80.0 mm
11 %

@Thickness 0.787 - 3.15 in
Typical Elongation
Modulus of Elasticity 69.0 GPa
10000 ksi
Thermal Properties Metric English Comments
CTE, linear 23.4 µm/m-°C

@Temperature 20.0 - 100 °C
13.0 µin/in-°F

@Temperature 68.0 - 212 °F
Thermal Conductivity 150 - 170 W/m-K
1040 - 1180 BTU-in/hr-ft²-°F
temper T651
Component Elements Properties Metric English Comments
Aluminum, Al 95.3 - 98.3 %
95.3 - 98.3 %
as balance
Chromium, Cr <= 0.25 %
<= 0.25 %
Copper, Cu <= 0.10 %
<= 0.10 %
Iron, Fe <= 0.50 %
<= 0.50 %
Magnesium, Mg 0.60 - 1.2 %
0.60 - 1.2 %
Manganese, Mn 0.40 - 1.0 %
0.40 - 1.0 %
Silicon, Si 0.70 - 1.3 %
0.70 - 1.3 %
Titanium, Ti <= 0.15 %
<= 0.15 %
Zinc, Zn <= 0.20 %
<= 0.20 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.00000360 - 0.00000420 ohm-cm
0.00000360 - 0.00000420 ohm-cm
temper T651