SABIC Innovative Plastics LNP LUBRICOMP RX85514 PA 66 (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP RX85514 PA 66 (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Lubricomp* RX85514 is a compound based on Nylon 66 resin containing Proprietary Filler(s).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.29 g/cc | 0.0466 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.012 - 0.014 cm/cm | 0.012 - 0.014 in/in | on Tensile Bar; SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 71.0 MPa | 10300 psi | 5 mm/min; ISO 527 |
| Tensile Strength, Yield | 43.0 MPa | 6240 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 5.3 % | 5.3 % | 5 mm/min; ISO 527 |
| Elongation at Yield | 3.3 % | 3.3 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 3.80 GPa | 551 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 106 MPa | 15400 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 3.30 GPa | 479 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 30.0 kJ/m² | 14.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 241 °C | 466 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 97.0 °C | 207 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
Users viewing this material also viewed the following:
- PolyOne Syncure™ V0045G RoHS Polyethylene, Crosslinked (XLPE)
- Omya HYDROCARB® PG-3 Calcium Carbonate
- Lehmann & Voss LUVOCOM® 1301-7629/EG PPS, linear, with carbon fiber
- Huntsman AVALON® 90 AKU Thermoplastic Polyurethane
- Gouda Vuurvast VIBRON 180 Dense Vibrating Refractory Castable
- SABIC Innovative Plastics LNP THERMOCOMP RX93402 PA 66
- Lubrizol Estane® ALR E60D Thermoplastic Polyurethane
- Eastman Drystar 0603 Copolyester
- Ashley Polymers Ashlene® 829L Nylon 6
- Resinlab® EP965 Black Unfilled Electronic Grade Epoxy Encapsulant
Copyright © lookpolymers.com All Rights Reserved