PolyOne Edgetek® MP-30GF/000 Modified PPO - 30% Glass Fiber Reinforced (discontinued **)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, 30% Glass Filled |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® MP-30GF/000 Modified PPO - 30% Glass Fiber Reinforced
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by PolyOne.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.28 g/cc | 0.0462 lb/in³ | ASTM D792 |
| Water Absorption | 0.060 % | 0.060 % | 24 hrs. ASTM D570 |
| Linear Mold Shrinkage | 0.0010 - 0.0030 cm/cm @Thickness 3.17 mm |
0.0010 - 0.0030 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 93 | 93 | ASTM D785 |
| Tensile Strength, Ultimate | 124 MPa | 18000 psi | ASTM D638 |
| Elongation at Break | 3.0 - 4.0 % | 3.0 - 4.0 % | ASTM D638 |
| Tensile Modulus | 7.60 GPa | 1100 ksi | ASTM D638 |
| Flexural Yield Strength | 165 MPa | 23900 psi | ASTM D790 |
| Flexural Modulus | 7.60 GPa | 1100 ksi | ASTM D790 |
| Izod Impact, Notched | 1.20 J/cm @Thickness 6.35 mm |
2.25 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 27.0 µm/m-°C @Temperature 20.0 °C |
15.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Thermal Conductivity | 0.190 W/m-K | 1.32 BTU-in/hr-ft²-°F | Cenco test |
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 154 °C | 309 °F | ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 282 - 304 °C | 540 - 579 °F | Stock |
| Mold Temperature | 93.0 °C | 199 °F | |
| Drying Temperature | 93.0 °C | 199 °F |
Users viewing this material also viewed the following:
- Iran Petrochemical (PCC) Arak 0410AA LLDPE (discontinued **)
- Lubrizol Advanced Materials PEARLCOAT® 127K Thermoplastic Polyurethane Elastomer
- Master Bond Mastersil 702 One Component, Room Temperature Curing Silicone Elastomer
- Unitika elitel UE3210 Polyester, Pellet
- Trelleborg E850 EPDM Rubber
- A. Schulman INVISION™ VX-5170UE Soft Touch Polyolefin Thermoplastic
- Lubrizol ESTANE® 5799 Ester Based Thermoplastic Polyurethane (European Grade)
- ExxonMobil Thermrex Series F-43
- ArcelorMittal 11 High formability steel for drawing, Hot rolled
- Owens Corning Glass Fiber Reinforced Polypropylene, 20 wt.% glass
Copyright © lookpolymers.com All Rights Reserved