- SABIC Innovative Plastics GELOY CR8510 ASA
SABIC Innovative Plastics GELOY CR8510 ASA
| Category | Polymer , Thermoplastic , ASA Polymer |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | GELOY |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics GELOY CR8510 ASA.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
ASA with outstanding UV exposure performance for both exterior and interior applications. F1 Rated.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.08 g/cc | 1.08 g/cc | ASTM D792 |
| Density | 1.07 g/cc | 0.0387 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.200 % | 0.200 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.50 % | 0.50 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0080 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 6.3 g/10 min @Load 10.0 kg, Temperature 220 °C |
6.3 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| 7.8 g/10 min @Load 3.80 kg, Temperature 280 °C |
7.8 g/10 min @Load 8.38 lb, Temperature 536 °F |
ASTM D1238 | |
| 11 g/10 min @Load 5.00 kg, Temperature 260 °C |
11 g/10 min @Load 11.0 lb, Temperature 500 °F |
ASTM D1238 | |
| Melt Index of Compound | 6.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
6.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
MVR [cm^3/10 min]; ISO 1133 |
| 10 g/10 min @Load 5.00 kg, Temperature 260 °C |
10 g/10 min @Load 11.0 lb, Temperature 500 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 93 | 93 | ASTM D785 |
| Tensile Strength at Break | 33.0 MPa | 4790 psi | Type I, 50 mm/min; ASTM D638 |
| 35.0 MPa | 5080 psi | 50 mm/min; ISO 527 | |
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | Type I, 50 mm/min; ASTM D638 |
| 43.0 MPa | 6240 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | 19 % | 19 % | 50 mm/min; ISO 527 |
| 60 % | 60 % | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Yield | 3.3 % | 3.3 % | 50 mm/min; ISO 527 |
| 3.6 % | 3.6 % | Type I, 50 mm/min; ASTM D638 | |
| Tensile Modulus | 1.97 GPa | 286 ksi | 5 mm/min; ASTM D638 |
| 2.04 GPa | 296 ksi | 1 mm/min; ISO 527 | |
| 2.07 GPa | 300 ksi | 50 mm/min; ASTM D638 | |
| Flexural Yield Strength | 64.0 MPa | 9280 psi | 2 mm/min; ISO 178 |
| 68.0 MPa | 9860 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 2.06 GPa | 299 ksi | 2 mm/min; ISO 178 |
| 2.17 GPa | 315 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 4.00 J/cm | 7.49 ft-lb/in | ASTM D256 |
| 0.600 J/cm @Temperature -30.0 °C |
1.12 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | 80*10*4; ISO 180/1A |
| 6.00 kJ/m² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 1.40 J/cm² | 6.66 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Dart Drop, Total Energy | 4.00 J @Temperature -30.0 °C |
2.95 ft-lb @Temperature -22.0 °F |
ASTM D3763 |
| 30.0 J @Temperature 23.0 °C |
22.1 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 84.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
46.7 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 84.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
46.7 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 95.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
52.8 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 95.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
52.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Hot Ball Pressure Test | <= 98.0 °C | <= 208 °F | IEC 60695-10-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 103 °C | 217 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 103 °C @Thickness 3.20 mm |
217 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 88.0 °C | 190 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| 89.0 °C | 192 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af | |
| 90.0 °C @Thickness 3.20 mm |
194 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 98.0 °C | 208 °F | Rate B/50; ASTM D1525 |
| 102 °C | 216 °F | Rate B/50; ISO 306 | |
| 105 °C | 221 °F | Rate B/120; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
UL 94 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gloss | 94 % | 94 % | untextured, 60 degrees; ASTM D523 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 26.1 kV/mm @Thickness 1.50 mm |
663 kV/in @Thickness 0.0591 in |
in oil; IEC 60243-1 |
| Dissipation Factor | 0.018 @Frequency 100000 Hz |
0.018 @Frequency 100000 Hz |
ASTM D150 |
| 0.026 @Frequency 1.00e+6 Hz |
0.026 @Frequency 1.00e+6 Hz |
ASTM D150 | |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| UV-light, water exposure/immersion | F1 | UL 746C |
Users viewing this material also viewed the following:
- Park Electrochemical Nelcote® E-766B Epoxy Prepreg, 120 E-Glass Reinforced
- Kingfa PC-S609 Toughened PC
- Styrolution Terblend® N NMX04 ABS/PA6 (Dry)
- Total PPH 10099 Polypropylene, Homopolymer
- A. Schulman POLYBATCH™ Blue 4535 Concentrate Based In Polyethylene
- Eurotec® Tecodur® PB70 GB20 NL PBT, 20% glass bead reinforced, natural
- Asahi Kasei Thermylene® P6-30FG-0877A 30% Glass Fiber Reinforced, UV Stabilized
- Axiall 2110 Wire & Cable Flexible PVC
- Cheng Yu Plastic ML1220 PC/PTFE, 20% Glass
Copyright © lookpolymers.com All Rights Reserved