SABIC Innovative Plastics GELOY CR3020 ASA
| Category | Polymer , Thermoplastic , ASA Polymer |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | GELOY |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics GELOY CR3020 ASA.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Low-gloss ASA for profile and capstock applications
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.07 g/cc | 1.07 g/cc | ASTM D792 |
| Density | 1.07 g/cc | 0.0387 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0055 - 0.0063 cm/cm @Thickness 3.20 mm |
0.0055 - 0.0063 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 5.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
5.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| 6.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
6.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 30.0 MPa | 4350 psi | Type I, 50 mm/min; ASTM D638 |
| 31.0 MPa | 4500 psi | 50 mm/min; ISO 527 | |
| Tensile Strength, Yield | 39.0 MPa | 5660 psi | Type I, 50 mm/min; ASTM D638 |
| 39.0 MPa | 5660 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | 23 % | 23 % | 50 mm/min; ISO 527 |
| 38 % | 38 % | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Yield | 3.4 % | 3.4 % | 50 mm/min; ISO 527 |
| 3.5 % | 3.5 % | Type I, 50 mm/min; ASTM D638 | |
| Tensile Modulus | 1.80 GPa | 261 ksi | 1 mm/min; ISO 527 |
| 1.84 GPa | 267 ksi | 5 mm/min; ASTM D638 | |
| Flexural Yield Strength | 56.0 MPa | 8120 psi | 2 mm/min; ISO 178 |
| 57.0 MPa | 8270 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 1.80 GPa | 261 ksi | 2 mm/min; ISO 178 |
| 1.86 GPa | 270 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.0800 J/cm | 0.150 ft-lb/in | ASTM D256 |
| 0.0100 J/cm @Temperature -30.0 °C |
0.0187 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 25.0 kJ/m² | 11.9 ft-lb/in² | 80*10*4; ISO 180/1A |
| 3.00 kJ/m² @Temperature -30.0 °C |
1.43 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Dart Drop, Total Energy | 4.00 J @Temperature 23.0 °C |
2.95 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 140 µm/m-°C @Temperature -40.0 - 40.0 °C |
77.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 200 µm/m-°C @Temperature -40.0 - 40.0 °C |
111 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 77.0 °C | 171 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 74.0 °C @Thickness 3.20 mm |
165 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 100 °C | 212 °F | Rate B/50; ASTM D1525 |
| 100 °C | 212 °F | Rate B/50; ISO 306 |
Users viewing this material also viewed the following:
- Quadrant EPP Ketron® CM 1030HT PEEK Polyetheretherketone, 30% carbon fiber reinforced, compression molded (ASTM Product Data Sheet)
- Parker Chomerics Tecknit NC-Consil® 750 Nickel Coated Graphite Filled Silicone Elastomer
- Zircar Ceramics ECO-27A Alumina-Silica Insulation
- Tra-Con Tra-Bond FS25
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 0.5 PHR Thanecure® ZM
- Colorite Polymers 7577 Non-Phthalate 77 Series Vinyl Compound
- Buckeye Polymers BP RPP 2020T Polypropylene, 20% Mineral Filled
- Huntsman PE6076 Blow Molding Polyethylene (discontinued **)
- Solvay Specialty Polymers Algoflon® 0.1 Mos PTFE; Molybdenum Disulfide Filled (discontinued **)
- Aaron Industries AVPE LD 300-1 MELT 20 Virgin Polyethylene
Copyright © lookpolymers.com All Rights Reserved