- Samsung Cheil Industries Infino® NH-1150HH PC/ABS, Unreinforced FR
Samsung Cheil Industries Infino® NH-1150HH PC/ABS, Unreinforced FR
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Infino® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Infino® NH-1150HH PC/ABS, Unreinforced FR.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.29 g/cc | 1.29 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0012 cm/cm @Thickness 3.20 mm |
0.0012 in/in @Thickness 0.126 in |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0019 cm/cm @Thickness 3.20 mm |
0.0019 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 6.0 g/10 min @Load 2.16 kg, Temperature 250 °C |
6.0 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
| 30 g/10 min @Load 10.0 kg, Temperature 220 °C |
30 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 110 | 110 | ASTM D785 |
| Tensile Strength at Break | 58.8 MPa | 8530 psi | 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 58.8 MPa | 8530 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 7.0 % | 7.0 % | 50 mm/min; ASTM D638 |
| Tensile Modulus | 3.33 GPa | 484 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 88.3 MPa | 12800 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 3.73 GPa | 540 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 0.785 J/cm @Thickness 6.35 mm |
1.47 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 0.785 J/cm @Thickness 3.17 mm |
1.47 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 81.0 °C @Thickness 6.40 mm |
178 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 94.0 °C | 201 °F | B/50; ISO R306 |
| Flammability, UL94 | V-0 @Thickness 1.20 mm |
V-0 @Thickness 0.0472 in |
Users viewing this material also viewed the following:
- Polimeri Europa Europrene Latice® 2620 Acrylonitrile-Butadiene Copolymer
- Lehmann & Voss LUVOCOM® 7/CF/30/BK Polyamide 610, with carbon fiber
- KaMin Polyfil® WC-426 Kaolin Clay - Calcined
- Techmer ES HiFill® PA6/6 GF60 TL10 60% Glass Filled
- Polyplastics Duranex® 2000 Polybutylene Terephthalate (PBT), High flow
- A. Schulman POLYBATCH™ Orange 1770E Concentrate Based In Polyethylene
- Hexcel® HexForce™ 220HT Fiber Glass Fabric
- Eurotec® Tecomid® NA40 NL FA50 PA6.6, unfilled, flame retardant - halogen free, natural
- Adamas Adalon® 237 PTFE, 25% Glass Fiber
- 3M FMV0E Void Polyester Label Products
Copyright © lookpolymers.com All Rights Reserved