- Cresset Powers Cress-Alon™ A2600 2.6 r.v. Compounding Grade Nylon 6, 50% RH
Cresset Powers Cress-Alon™ A2600 2.6 r.v. Compounding Grade Nylon 6, 50% RH
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | Cresset Powers, Ltd |
| Trade Name | Cress-Alon™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Cresset Powers Cress-Alon™ A2600 2.6 r.v. Compounding Grade Nylon 6, 50% RH.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Neat resin, for compounding.Information provided by Cresset Powers Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 - 1.14 g/cc | 0.0405 - 0.0412 lb/in³ | ASTM D792 |
| Apparent Bulk Density | >= 0.659 g/cc | >= 0.0238 lb/in³ | |
| Viscosity Measurement | 2.6 | 2.6 | Relative Viscosity |
| Melt Flow | 14 - 20 g/10 min @Load 2.16 kg, Temperature 230 °C |
14 - 20 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 - 224 °C | 428 - 435 °F | ASTM DSC |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 55.0 °C | >= 131 °F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Moisture Content | <= 0.080 % | <= 0.080 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Extractables, wt% | <0.4 |
Users viewing this material also viewed the following:
- Multibase Multi-Flex® TPE A 8599 BLK
- Multibase Multi-Pro® 3010 X Black Polypropylene
- Precision Polymer Engineering V95X Fluoroelastomer Compound
- SABIC Innovative Plastics Cycoloy® FXC813SK PC+ABS (Europe-Africa-Middle East)
- Lehmann & Voss LUVOCOM® 1105-8354 PEEK, with carbon fiber
- Lucas-Milhaupt Silvaloy® A56T Brazing Alloy
- H.C. Starck Ultra 76 Alloy (Ta 2.5%W)
- Teijin Multilon T-2711 Standard, Automobile Part Series PC/ABS Polymer Alloy
- 3M 5181 General Purpose PTFE Skived Film Tapes
Copyright © lookpolymers.com All Rights Reserved