SABIC Innovative Plastics NORYL PPX PPX7110 PPE+PP (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl PPX |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL PPX PPX7110 PPE+PP (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PPE+PP blend. High Impact, Good Heat Resistance
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.970 g/cc | 0.970 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0080 - 0.012 cm/cm @Thickness 3.20 mm |
0.0080 - 0.012 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 10.6 g/10 min @Load 5.00 kg, Temperature 260 °C |
10.6 g/10 min @Load 11.0 lb, Temperature 500 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 32.0 MPa | 4640 psi | Type I, 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 35.0 MPa | 5080 psi | Type I, 50 mm/min; ASTM D638 |
| Elongation at Break | 195 % | 195 % | Type I, 50 mm/min; ASTM D638 |
| Elongation at Yield | 6.5 % | 6.5 % | Type I, 50 mm/min; ASTM D638 |
| Tensile Modulus | 1.34 GPa | 194 ksi | 50 mm/min; ASTM D638 |
| Flexural Yield Strength | 51.0 MPa | 7400 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 1.55 GPa | 225 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 4.37 J/cm | 8.19 ft-lb/in | ASTM D256 |
| 1.49 J/cm @Temperature -30.0 °C |
2.79 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Dart Drop, Total Energy | 27.0 J @Temperature -30.0 °C |
19.9 ft-lb @Temperature -22.0 °F |
ASTM D3763 |
| 37.0 J @Temperature 23.0 °C |
27.3 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 81.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
45.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 112 µm/m-°C @Temperature -40.0 - 40.0 °C |
62.2 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 113 °C @Thickness 3.20 mm |
235 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 77.0 °C @Thickness 3.20 mm |
171 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Vicat Softening Point | 138 °C | 280 °F | Rate B/50; ASTM D1525 |
| UL RTI, Electrical | 50.0 °C | 122 °F | UL 746B |
| UL RTI, Mechanical with Impact | 50.0 °C | 122 °F | UL 746B |
| UL RTI, Mechanical without Impact | 50.0 °C | 122 °F | UL 746B |
| Flammability, UL94 | HB @Thickness 1.52 mm |
HB @Thickness 0.0598 in |
UL 94 |
Users viewing this material also viewed the following:
- RheTech Products G13P100-598UV 13% Glass Fiber Reinforced Polypropylene, UV Stabilized, (NH-293L) Seagull Gray
- Plenco 51240 PET, Pellet, Injection Molded, Natural Color (discontinued **)
- Qualchem Danamid FGFHUV-30 Polyamide 6, 30% Glass Fiber
- SABIC Innovative Plastics NORYL V03505 PPE+HIPS (Europe-Africa-Middle East)
- Silberline EternaBrite® 301-1
- Teknor Apex Chemlon® 275H Nylon 6, Copolymer, Impact Modified
- Universal Wire Works BNi-4 (AMS 4779) Nickel Base Brazing Filler Metal
- DSM Arnite® TV4 240 PBT-20% Glass Reinforced (European and Asian Grade)
- CLAL-MSX DECLAFOR® 1015 TD1 Rod quenched/Cold Rolled Copper Alloy
- Bhansali Engineering Abstron IMG-1115 Glass Reinforced Grade
Copyright © lookpolymers.com All Rights Reserved