SABIC Innovative Plastics Cycoloy® XCM851 PC+ABS

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Cycoloy®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Cycoloy® XCM851 PC+ABS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
High heat PC/ABS blend offering high modulus / low CTE and good practical impact
Physical Properties Metric English Comments
Specific Gravity 1.30 g/cc
1.30 g/cc
ASTM D792
Density 1.30 g/cc
0.0470 lb/in³
ISO 1183
Moisture Absorption 0.0100 %
0.0100 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.20 %
0.20 %
ISO 62
Linear Mold Shrinkage, Flow 0.0030 - 0.0050 cm/cm

@Thickness 3.20 mm
0.0030 - 0.0050 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 12 g/10 min

@Load 5.00 kg,
Temperature 260 °C
12 g/10 min

@Load 11.0 lb,
Temperature 500 °F
ASTM D1238
Melt Index of Compound 9.0 g/10 min

@Load 5.00 kg,
Temperature 260 °C
9.0 g/10 min

@Load 11.0 lb,
Temperature 500 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 35.0 MPa
5080 psi
Type I, 5 mm/min; ASTM D638
45.0 MPa
6530 psi
5 mm/min; ISO 527
Tensile Strength, Yield 55.0 MPa
7980 psi
5 mm/min; ISO 527
60.0 MPa
8700 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 10 %
10 %
5 mm/min; ISO 527
12 %
12 %
Type I, 5 mm/min; ASTM D638
Elongation at Yield 4.0 %
4.0 %
Type I, 5 mm/min; ASTM D638
4.0 %
4.0 %
5 mm/min; ISO 527
Tensile Modulus 4.60 GPa
667 ksi
1 mm/min; ISO 527
4.75 GPa
689 ksi
5 mm/min; ASTM D638
Flexural Yield Strength 100 MPa
14500 psi
2 mm/min; ISO 178
108 MPa
15700 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 4.40 GPa
638 ksi
2 mm/min; ISO 178
4.55 GPa
660 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 1.00 J/cm
1.87 ft-lb/in
ASTM D256
0.800 J/cm

@Temperature -30.0 °C
1.50 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Notched (ISO) 12.0 kJ/m²
5.71 ft-lb/in²
80*10*3; ISO 180/1A
9.00 kJ/m²

@Temperature -30.0 °C
4.28 ft-lb/in²

@Temperature -22.0 °F
80*10*3; ISO 180/1A
Izod Impact, Unnotched (ISO) NB
NB
80*10*3; ISO 180/1U
Charpy Impact Unnotched NB
NB
Edgew 80*10*3 sp=62mm; ISO 179/1eU
Charpy Impact, Notched 1.50 J/cm²
7.14 ft-lb/in²
Edgew 80*10*3 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 60.0 J

@Temperature 23.0 °C
44.3 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 41.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
22.8 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
41.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
22.8 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 56.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
31.1 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
56.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
31.1 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 122 °C
252 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
119 °C

@Thickness 3.20 mm
246 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 138 °C
280 °F
Rate B/50; ASTM D1525
139 °C
282 °F
Rate B/50; ISO 306
140 °C
284 °F
Rate B/120; ISO 306