DuPont Teijin Films Mylar® LB Polyester Film, 75 Gauge (19 µm)

Category	Polymer , Film , Thermoplastic , Polyester, TP , Polyester Film
Manufacturer	DuPont Teijin Films (DTF)
Trade Name	Mylar®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	DuPont Teijin Films Mylar® LB Polyester Film, 75 Gauge (19 µm).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Data provided by DuPont Packaging Polymers.An uncoated, transparent polyester film designed for use as a component of a lamination. Standard thickness offered include 48, 75, and 92 gauges. Varieties with enhanced surface characteristics for bonding by inks, primers, and adhesives. A basic lamination would combine plain or printed LB with a heat sealable ply consisting of LDPE, LLDPE, EVA, ionomer, acid copolymer, PVC, or other materials using adhesive or extrusion laminating techniques.

Physical Properties	Metric	English	Comments
Density	1.40 g/cc	0.0506 lb/in³	Average value for Mylar® films.
Moisture Vapor Transmission	0.600 cc-mm/m²-24hr-atm	1.52 cc-mil/100 in²-24hr-atm	ASTM E96 Procedure E
Water Vapor Transmission	30.0 g/m²/day	1.93 g/100 in²/day	ASTM E96 Procedure E
Oxygen Transmission	2.10 cc-mm/m²-24hr-atm	5.33 cc-mil/100 in²-24hr-atm	or 110 cc/m²-24hr-atm for the film. ASTM D3985

Mechanical Properties	Metric	English	Comments
Film Elongation at Break, MD	130 %	130 %	ASTM D882
Film Elongation at Break, TD	100 %	100 %	ASTM D882
Modulus of Elasticity	3.79 GPa	550 ksi	(stiffness), ASTM D882
Tear Strength Test	400	400	Graves, g; ASTM D1004
Film Tensile Strength at Break, MD	200 MPa	29000 psi	ASTM D882
Film Tensile Strength at Break, TD	242 MPa	35100 psi	ASTM D882

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	121 °C	250 °F	May be used to contain foods during baking above this temperature.
Shrinkage, MD	2.2 % @Temperature 150 °C, Time 1800 sec	2.2 % @Temperature 302 °F, Time 0.500 hour	Film shrinkage in oven.
Shrinkage, TD	1.1 % @Temperature 150 °C, Time 1800 sec	1.1 % @Temperature 302 °F, Time 0.500 hour	Film shrinkage in oven.

Optical Properties	Metric	English	Comments
Haze	6.5 %	6.5 %	ASTM D1003
Gloss	180 %	180 %	20°; ASTM D2457
Transmission, Visible	73 %	73 %	% Clarity; ASTM D1746