- Samsung Cheil Industries Starex® BF-0679P MABS, Unreinforced Scratch Resistant
Samsung Cheil Industries Starex® BF-0679P MABS, Unreinforced Scratch Resistant
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Starex® BF-0679P MABS, Unreinforced Scratch Resistant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Scratch resistant material that is used for the exterior material of flat TVInformation provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.13 g/cc | 1.13 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm @Thickness 3.20 mm |
0.0040 in/in @Thickness 0.126 in |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0050 cm/cm @Thickness 3.20 mm |
0.0050 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 13 g/10 min @Load 10.0 kg, Temperature 220 °C |
13 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 116 | 116 | ASTM D785 |
| Tensile Strength at Break | 40.2 MPa | 5830 psi | 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 49.0 MPa | 7110 psi | 5 mm/min; ASTM D638 |
| Elongation at Break | 18 % | 18 % | 5 mm/min; ASTM D638 |
| Tensile Modulus | 2.45 GPa | 356 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 71.6 MPa | 10400 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 2.36 GPa | 343 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 0.785 J/cm @Thickness 6.35 mm |
1.47 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 0.922 J/cm @Thickness 3.17 mm |
1.73 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 94.0 °C @Thickness 6.40 mm |
201 °F @Thickness 0.252 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C @Thickness 6.40 mm |
185 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 97.0 °C | 207 °F | B/50; ISO R306 |
| 100 °C | 212 °F | B/120; ISO R306 | |
| Flammability, UL94 | HB @Thickness 1.50 - 3.00 mm |
HB @Thickness 0.0591 - 0.118 in |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Pencil Hardness | 2H | 500g, JIS K 5401 |
Users viewing this material also viewed the following:
- PolyOne OnFlex™ V 3040D-S0093 Thermoplastic Elastomer (TPE)
- SABIC Innovative Plastics Lexan® HPS1R PC (Asia Pacific)
- Polymer Resources PC-BR1-[color]-5 Polycarbonate, Branched, Food Contact
- Eastman D4028-F Polyethylene (discontinued **)
- Karina Micro-Ex 4648/1-EXPO Black PVC Compound
- Mallard Creek Polymers TYLAC® 814 SBR Emulsion
- Ferro EG 0002 Glazes and Sealants
- Lucas-Milhaupt Silvacore® A50N Flux Cored Brazing Alloy
- Samyang Triloy® 170 PC/PBT alloy
- Ametek High Purity Nickel Strip 899L Annealed
Copyright © lookpolymers.com All Rights Reserved