SABIC Innovative Plastics Cycoloy® CY6009 PC+ABS (Asia Pacific)

Category	Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	Cycoloy®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics Cycoloy® CY6009 PC+ABS (Asia Pacific).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

CY6009 is a flame retardant (FR) PC+ABS blend with non-brominated and non-chlorinated FR systems. Its excellent flow together with balanced properties and thin wall 5VB capability at less than 2 mm is designed for various thin wall applications.

Physical Properties	Metric	English	Comments
Specific Gravity	1.19 g/cc	1.19 g/cc	ASTM D792
Density	1.19 g/cc	0.0430 lb/in³	ISO 1183
Moisture Absorption	0.200 %	0.200 %	23°C / 50% RH; ISO 62
Water Absorption at Saturation	0.20 %	0.20 %	ISO 62
Linear Mold Shrinkage, Flow	0.0040 - 0.0060 cm/cm @Thickness 3.20 mm	0.0040 - 0.0060 in/in @Thickness 0.126 in	SABIC Method
Melt Flow	28 g/10 min @Load 2.16 kg, Temperature 260 °C	28 g/10 min @Load 4.76 lb, Temperature 500 °F	ASTM D1238
Melt Index of Compound	25 g/10 min @Load 2.16 kg, Temperature 260 °C	25 g/10 min @Load 4.76 lb, Temperature 500 °F	MVR [cm^3/10 min]; ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	40.0 MPa	5800 psi	Type I, 50 mm/min; ASTM D638
	41.0 MPa	5950 psi	50 mm/min; ISO 527
Tensile Strength, Yield	62.0 MPa	8990 psi	Type I, 50 mm/min; ASTM D638
	63.0 MPa	9140 psi	50 mm/min; ISO 527
Elongation at Break	51 %	51 %	50 mm/min; ISO 527
	80 %	80 %	Type I, 50 mm/min; ASTM D638
Elongation at Yield	3.8 %	3.8 %	50 mm/min; ISO 527
	3.9 %	3.9 %	Type I, 50 mm/min; ASTM D638
Tensile Modulus	2.75 GPa	399 ksi	1 mm/min; ISO 527
	2.80 GPa	406 ksi	50 mm/min; ASTM D638
Flexural Yield Strength	92.0 MPa	13300 psi	1.3 mm/min, 50 mm span; ASTM D790
	94.0 MPa	13600 psi	2 mm/min; ISO 178
Flexural Modulus	2.70 GPa	392 ksi	1.3 mm/min, 50 mm span; ASTM D790
	2.75 GPa	399 ksi	2 mm/min; ISO 178
Izod Impact, Notched	1.10 J/cm	2.06 ft-lb/in	ASTM D256
	0.550 J/cm @Temperature -30.0 °C	1.03 ft-lb/in @Temperature -22.0 °F	ASTM D256
Izod Impact, Notched (ISO)	7.00 kJ/m²	3.33 ft-lb/in²	80103; ISO 180/1A
	5.00 kJ/m² @Temperature -30.0 °C	2.38 ft-lb/in² @Temperature -22.0 °F	80103; ISO 180/1A
Charpy Impact, Notched	1.00 J/cm²	4.76 ft-lb/in²	Edgew 80103 sp=62mm; ISO 179/1eA
	0.700 J/cm² @Temperature -30.0 °C	3.33 ft-lb/in² @Temperature -22.0 °F	Edgew 80103 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy	20.0 J @Temperature 23.0 °C	14.8 ft-lb @Temperature 73.4 °F	ASTM D3763

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	70.0 µm/m-°C @Temperature -40.0 - 40.0 °C	38.9 µin/in-°F @Temperature -40.0 - 104 °F	ASTM E 831
	70.0 µm/m-°C @Temperature -40.0 - 40.0 °C	38.9 µin/in-°F @Temperature -40.0 - 104 °F	ISO 11359-2
CTE, linear, Transverse to Flow	70.0 µm/m-°C @Temperature -40.0 - 40.0 °C	38.9 µin/in-°F @Temperature -40.0 - 104 °F	ASTM E 831
	70.0 µm/m-°C @Temperature -40.0 - 40.0 °C	38.9 µin/in-°F @Temperature -40.0 - 104 °F	ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi)	79.0 °C	174 °F	Flatw 80104 sp=64mm; ISO 75/Af
	80.0 °C @Thickness 6.40 mm	176 °F @Thickness 0.252 in	unannealed; ASTM D648
Vicat Softening Point	90.0 °C	194 °F	Rate B/50; ASTM D1525
	90.0 °C	194 °F	Rate B/50; ISO 306
	94.0 °C	201 °F	Rate B/120; ISO 306
Flammability, UL94	V-1 @Thickness 1.50 mm	V-1 @Thickness 0.0591 in	UL 94
	5VB @Thickness 1.80 mm	5VB @Thickness 0.0709 in	UL 94