DuPont Performance Polymers VTR 8605 (GF-S), VTR 8600 (GF-S) 8605/VTR 8600 Blend (discontinued **)
| Category | Polymer , Thermoset , Fluoropolymer, TS , Thermoset Fluoroelastomer , Rubber or Thermoset Elastomer (TSE) |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Performance Polymers VTR 8605 (GF-S), VTR 8600 (GF-S) 8605/VTR 8600 Blend
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
FormulationVTR 8605
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 74 | 74 | Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
| Tensile Strength, Ultimate | 18.7 MPa | 2710 psi | Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
| Elongation at Break | 237 % | 237 % | Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
| Modulus of Elasticity | 0.00106 GPa | 0.154 ksi | 10% Modulus, Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
| 100% Modulus | 0.00660 GPa | 0.957 ksi | Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
| Compression Set | 14 % @Temperature 200 °C |
14 % @Temperature 392 °F |
Method B, O-rings 22 hr at 200°C (Post Cured 2 hr at 232°C) |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Glass Transition Temp, Tg | -5.40 °C | 22.3 °F | MDSC, postcured |
Users viewing this material also viewed the following:
- Pacific Sintered Materials FN-250-S Nickel Iron Powdered Metal
- Mitsui ADMER® NF528A PE Type Polyolefin
- SABIC Innovative Plastics LNP VERTON MV006SU PP (Europe-Africa-Middle East)
- Eurostar Staramide RF00AES PA66/6, 50% Glass Filled, Injection Molded
- Entec Hypro™ PPC-T30 Copolymer Polypropylene, 30% Talc Reinforced
- Addiplast Addilene H 490 M20S Flame Retardant Polypropylene, 20% Mineral Filled
- Carpenter MP35N* Ni-Co-Cr-Mo Alloy, 25% Cold Reduction
- Arlon Thermabond® 99730N015 0.015" (0.381 mm) Uncured Silicone Rubber with PTFE Coated Fiberglass Carrier
- Aremco Aremco-Bond™ 820 High Performance Epoxide
- A. Schulman ComAlloy Aqualoy® 143 Polypropylene, Glass Reinforced, Chemically Coupled
Copyright © lookpolymers.com All Rights Reserved