Beijing Chemical Industry KAIFA® S-114 PPS Resin
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS), Mineral/Glass-Fiber Filled |
| Manufacturer | Beijing Chemical Industry Research Institute (Group) |
| Trade Name | KAIFA® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Beijing Chemical Industry KAIFA® S-114 PPS Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Glass fiber reinforcedInformation provided by Beijing Chemical Industry Research Institute (Group)
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.67 g/cc | 0.0603 lb/in³ | ASTM D792 |
| Water Absorption | 0.050 % | 0.050 % | 24 hr; ASTM D570 |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 150 MPa | 21800 psi | ASTM D638 |
| Elongation at Break | 0.80 % | 0.80 % | ASTM D638 |
| Flexural Strength | 185 MPa | 26800 psi | ASTM D790 |
| Flexural Modulus | 1.20 GPa | 174 ksi | ASTM D790 |
| Charpy Impact Unnotched | 2.50 J/cm² | 11.9 ft-lb/in² | ISO179 |
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | ISO179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 260 °C | 500 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 3.20 mm |
V-0 @Thickness 0.126 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.8 @Frequency 1e+6 Hz |
3.8 @Frequency 1e+6 Hz |
ASTM D150 |
| Dielectric Strength | 17.0 kV/mm @Thickness 2.00 mm |
432 kV/in @Thickness 0.0787 in |
ASTM D149 |
| Dissipation Factor | 0.0020 @Frequency 1e+6 Hz |
0.0020 @Frequency 1e+6 Hz |
ASTM D150 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 280 - 315 °C | 536 - 599 °F | Injection Temp. |
| Mold Temperature | 135 - 150 °C | 275 - 302 °F | |
| Drying Temperature | 130 °C | 266 °F | |
| Dry Time | 4 hour | 4 hour | |
| Injection Pressure | 60.0 MPa | 8700 psi |
Users viewing this material also viewed the following:
- Osprey Metals 4140 Low Alloy Steel Powder (Grade 90% - 22)
- SABIC Innovative Plastics Cycoloy® CE1821 PC+ABS (Asia Pacific)
- Plastcom SLOVALEN PH 92 T 30 PP, 30% mineral filling
- Lehmann & Voss LUVOCOM® 20-0664 Polyphthalamide, with PTFE, lubricant modified
- MetalTek C18100 Chrome Zirc Copper High Conductivity
- Spartech Polycast SAR (Super Abrasion Resistant) Cell Cast Acrylic
- Teknor Apex Uniprene® UN-2023 Thermoplastic Elastomer
- A. Schulman POLYBATCH™ Green 3373 Concentrate Based In Polyethylene
- EMS-Grivory Grivory® HTV-6H1 nat PA6T/6I-GF60
- Dow SE SLR-4630 Solution polymerized Styrene Butadiene Rubber (S-SBR)
Copyright © lookpolymers.com All Rights Reserved