SABIC Innovative Plastics Cycoloy® CM6240 PC+ABS (Asia Pacific)

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Cycoloy®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Cycoloy® CM6240 PC+ABS (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
CYCOLOY CM6240 resin is a flame retardant PC/ABS blend featuring balanced properties of high modulus, good flow and ductility. It is of Br- & Cl-free flame retardant systems intended to meet thin wall flame resistance and various environmental requirements.
Physical Properties Metric English Comments
Specific Gravity 1.30 g/cc
1.30 g/cc
ASTM D792
Density 1.30 g/cc
0.0470 lb/in³
ISO 1183
Moisture Absorption 0.0300 %
0.0300 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.10 %
0.10 %
ISO 62
Linear Mold Shrinkage, Flow 0.0033 cm/cm
0.0033 in/in
SABIC Method
0.0030 - 0.0040 cm/cm

@Thickness 3.20 mm
0.0030 - 0.0040 in/in

@Thickness 0.126 in
SABIC Method
Linear Mold Shrinkage, Transverse 0.0038 cm/cm
0.0038 in/in
SABIC Method
Melt Flow 16.5 g/10 min

@Load 2.16 kg,
Temperature 260 °C
16.5 g/10 min

@Load 4.76 lb,
Temperature 500 °F
ASTM D1238
Melt Index of Compound 15 g/10 min

@Load 2.16 kg,
Temperature 260 °C
15 g/10 min

@Load 4.76 lb,
Temperature 500 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 29.0 MPa
4210 psi
5 mm/min; ISO 527
40.0 MPa
5800 psi
Type I, 5 mm/min; ASTM D638
Tensile Strength, Yield 55.0 MPa
7980 psi
Type I, 5 mm/min; ASTM D638
56.0 MPa
8120 psi
5 mm/min; ISO 527
Elongation at Break 25 %
25 %
5 mm/min; ISO 527
35 %
35 %
Type I, 5 mm/min; ASTM D638
Elongation at Yield 3.0 %
3.0 %
Type I, 5 mm/min; ASTM D638
3.0 %
3.0 %
5 mm/min; ISO 527
Tensile Modulus 4.35 GPa
631 ksi
5 mm/min; ASTM D638
4.46 GPa
647 ksi
1 mm/min; ISO 527
Flexural Yield Strength 96.0 MPa
13900 psi
1.3 mm/min, 50 mm span; ASTM D790
101 MPa
14600 psi
2 mm/min; ISO 178
Flexural Modulus 4.40 GPa
638 ksi
1.3 mm/min, 50 mm span; ASTM D790
4.51 GPa
654 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.860 J/cm
1.61 ft-lb/in
ASTM D256
0.600 J/cm

@Temperature -30.0 °C
1.12 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Notched (ISO) 7.00 kJ/m²
3.33 ft-lb/in²
80*10*4; ISO 180/1A
7.00 kJ/m²

@Temperature -30.0 °C
3.33 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
Charpy Impact, Notched 0.600 J/cm²
2.86 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 35.0 J

@Temperature -30.0 °C
25.8 ft-lb

@Temperature -22.0 °F
ASTM D3763
56.0 J

@Temperature 23.0 °C
41.3 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 48.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
26.7 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
49.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
27.2 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow 63.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
35.0 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
64.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
35.6 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
Deflection Temperature at 1.8 MPa (264 psi) 86.0 °C
187 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
90.0 °C

@Thickness 6.40 mm
194 °F

@Thickness 0.252 in
unannealed; ASTM D648
Vicat Softening Point 97.0 °C
207 °F
Rate B/50; ASTM D1525
97.0 °C
207 °F
Rate B/50; ISO 306
100 °C
212 °F
Rate B/120; ISO 306
Flammability, UL94 V-0

@Thickness 0.800 mm
V-0

@Thickness 0.0315 in
UL 94 by SABIC-IP
5VB

@Thickness 1.50 mm
5VB

@Thickness 0.0591 in
UL 94 by SABIC-IP