SABIC Innovative Plastics Valox® ENH4550 PBT (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Valox®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Valox® ENH4550 PBT (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
25% GF reinforced, Non-Brominated & Non-Chlorinated Flame Retardant, PBT resin.
Physical Properties Metric English Comments
Specific Gravity 1.52 g/cc
1.52 g/cc
ASTM D792
Density 1.52 g/cc
0.0549 lb/in³
ISO 1183
Filler Content 25 %
25 %
ASTM D229
Moisture Absorption 0.0600 %
0.0600 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.23 %
0.23 %
ISO 62
Viscosity 160000 cP
160000 cP
Melt Viscosity, 260°C, 1500 sec-1; ISO 11443
210000 cP
210000 cP
Melt Viscosity, 250°C, 1500 sec-1; ISO 11443
Linear Mold Shrinkage, Flow 0.0010 - 0.0050 cm/cm
0.0010 - 0.0050 in/in
on Tensile Bar; SABIC Method
0.0010 - 0.0050 cm/cm

@Thickness 3.20 mm
 0.0010 - 0.0050 in/in

@Thickness 0.126 in
 SABIC Method
Linear Mold Shrinkage, Transverse 0.0060 - 0.012 cm/cm
0.0060 - 0.012 in/in
on Tensile Bar; SABIC Method
0.0050 - 0.011 cm/cm

@Thickness 3.20 mm
 0.0050 - 0.011 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 25 g/10 min

@Load 5.00 kg,
Temperature 265 °C
 25 g/10 min

@Load 11.0 lb,
Temperature 509 °F
 ASTM D1238
27 g/10 min

@Load 5.00 kg,
Temperature 250 °C
 27 g/10 min

@Load 11.0 lb,
Temperature 482 °F
 ASTM D1238
Melt Index of Compound 17 g/10 min

@Load 5.00 kg,
Temperature 265 °C
 17 g/10 min

@Load 11.0 lb,
Temperature 509 °F
 MVR [cm^3/10 min]; ISO 1133
20 g/10 min

@Load 5.00 kg,
Temperature 250 °C
 20 g/10 min

@Load 11.0 lb,
Temperature 482 °F
 MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell R 124
124
ISO 2039-2
Hardness, H358/30 174 MPa
25200 psi
ISO 2039-1
Tensile Strength at Break 112 MPa
16200 psi
5 mm/min; ISO 527
115 MPa
16700 psi
Type I, 5 mm/min; ASTM D638
Tensile Strength, Yield 112 MPa
16200 psi
5 mm/min; ISO 527
115 MPa
16700 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 2.0 %
2.0 %
Type I, 5 mm/min; ASTM D638
2.0 %
2.0 %
5 mm/min; ISO 527
2.0 %
2.0 %
Flexural Strain, break, 2 mm/min; ISO 178
Elongation at Yield 2.0 %
2.0 %
Type I, 5 mm/min; ASTM D638
2.0 %
2.0 %
5 mm/min; ISO 527
Tensile Modulus 10.3 GPa
1490 ksi
5 mm/min; ASTM D638
10.4 GPa
1510 ksi
1 mm/min; ISO 527
Flexural Strength 165 MPa
23900 psi
1.3 mm/min, 50 mm span; ASTM D790
175 MPa
25400 psi
2 mm/min; ISO 178
Flexural Yield Strength 165 MPa
23900 psi
1.3 mm/min, 50 mm span; ASTM D790
175 MPa
25400 psi
2 mm/min; ISO 178
Flexural Modulus 8.50 GPa
1230 ksi
1.3 mm/min, 50 mm span; ASTM D790
9.20 GPa
1330 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.700 J/cm
1.31 ft-lb/in
ASTM D256
0.700 J/cm

@Temperature 0.000 °C
 1.31 ft-lb/in

@Temperature 32.0 °F
 ASTM D256
0.700 J/cm

@Temperature -30.0 °C
 1.31 ft-lb/in

@Temperature -22.0 °F
 ASTM D256
Izod Impact, Unnotched 5.50 J/cm
10.3 ft-lb/in
ASTM D4812
5.50 J/cm

@Temperature -30.0 °C
 10.3 ft-lb/in

@Temperature -22.0 °F
 ASTM D4812
Izod Impact, Notched (ISO) 8.00 kJ/m²
3.81 ft-lb/in²
80*10*4; ISO 180/1A
8.00 kJ/m²

@Temperature 0.000 °C
 3.81 ft-lb/in²

@Temperature 32.0 °F
 80*10*4; ISO 180/1A
8.00 kJ/m²

@Temperature -30.0 °C
 3.81 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 40.0 kJ/m²
19.0 ft-lb/in²
80*10*4; ISO 180/1U
38.0 kJ/m²

@Temperature -30.0 °C
 18.1 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1U
Charpy Impact Unnotched 4.50 J/cm²
21.4 ft-lb/in²
ISO 179/2C
4.00 J/cm²

@Temperature -30.0 °C
 19.0 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/2C
Charpy Impact, Notched 0.500 J/cm²
2.38 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
0.900 J/cm²
4.28 ft-lb/in²
ISO 179/2C
0.900 J/cm²

@Temperature -30.0 °C
 4.28 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/2C
Dart Drop, Total Energy 6.00 J

@Temperature 23.0 °C
 4.43 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
ASTM D257
1.00e+15 ohm-cm
1.00e+15 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
ROA; IEC 60093
Dielectric Constant 3.4

@Frequency 1.00e+6 Hz
 3.4

@Frequency 1.00e+6 Hz
 ASTM D150
3.4

@Frequency 1.00e+6 Hz
 3.4

@Frequency 1.00e+6 Hz
 IEC 60250
Dielectric Strength 19.0 kV/mm

@Thickness 3.20 mm
 483 kV/in

@Thickness 0.126 in
 in oil; ASTM D149
19.0 kV/mm

@Thickness 3.20 mm
 483 kV/in

@Thickness 0.126 in
 in oil; IEC 60243-1
21.0 kV/mm

@Thickness 3.20 mm
 533 kV/in

@Thickness 0.126 in
 in air; ASTM D149
24.0 kV/mm

@Thickness 1.60 mm
 610 kV/in

@Thickness 0.0630 in
 in oil; ASTM D149
24.0 kV/mm

@Thickness 1.60 mm
 610 kV/in

@Thickness 0.0630 in
 in oil; IEC 60243-1
30.0 kV/mm

@Thickness 0.800 mm
 762 kV/in

@Thickness 0.0315 in
 in oil; IEC 60243-1
30.0 kV/mm

@Thickness 0.800 mm
 762 kV/in

@Thickness 0.0315 in
 in oil; ASTM D149
Dissipation Factor 0.12

@Frequency 1.00e+6 Hz
 0.12

@Frequency 1.00e+6 Hz
 ASTM D150
0.12

@Frequency 1.00e+6 Hz
 0.12

@Frequency 1.00e+6 Hz
 IEC 60250
Arc Resistance 60 - 120 sec
60 - 120 sec
Tungsten; ASTM D495
Comparative Tracking Index 300 V
300 V
IEC 60112
250 - 400 V
250 - 400 V
UL 746A
Hot Wire Ignition, HWI >= 120 sec
>= 120 sec
UL 746A