SABIC Innovative Plastics Cycoloy® CH6410 PC+ABS (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Cycoloy®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Cycoloy® CH6410 PC+ABS (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
CH6410 is a high heat, impact modified PC resin, with nonbrominated, nonchlorinated flame retardant system. Limited colors only.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Physical Properties Metric English Comments
Density 1.20 g/cc
0.0434 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
on tensile bar; SABIC Method
Melt Flow 16 g/10 min

@Load 5.00 kg,
Temperature 260 °C
 16 g/10 min

@Load 11.0 lb,
Temperature 500 °F
 [cm^3/10 min] Melt Volume Rate; ISO 1133
Mechanical Properties Metric English Comments
Hardness, H358/30 100 MPa
14500 psi
ISO 2039-1
Tensile Strength at Break 55.0 MPa
7980 psi
50 mm/min; ISO 527
Tensile Strength, Yield 63.0 MPa
9140 psi
50 mm/min; ISO 527
Elongation at Break 95 %
95 %
50 mm/min; ISO 527
Elongation at Yield 5.0 %
5.0 %
50 mm/min; ISO 527
Tensile Modulus 2.30 GPa
334 ksi
1 mm/min; ISO 527
Flexural Yield Strength 90.0 MPa
13100 psi
2 mm/min; ISO 178
Flexural Modulus 2.40 GPa
348 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 15.0 kJ/m²

@Temperature -30.0 °C
 7.14 ft-lb/in²

@Temperature -22.0 °F
 80*10*3; ISO 180/1A
15.0 kJ/m²

@Temperature -30.0 °C
 7.14 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
19.0 kJ/m²

@Temperature 0.000 °C
 9.04 ft-lb/in²

@Temperature 32.0 °F
 80*10*4; ISO 180/1A
50.0 kJ/m²

@Temperature 23.0 °C
 23.8 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1A
55.0 kJ/m²

@Temperature 23.0 °C
 26.2 ft-lb/in²

@Temperature 73.4 °F
 80*10*3; ISO 180/1A
Charpy Impact, Notched 1.50 J/cm²

@Temperature -30.0 °C
 7.14 ft-lb/in²

@Temperature -22.0 °F
 V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA
1.50 J/cm²

@Temperature -30.0 °C
 7.14 ft-lb/in²

@Temperature -22.0 °F
 V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA
5.50 J/cm²

@Temperature 23.0 °C
 26.2 ft-lb/in²

@Temperature 73.4 °F
 V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA
5.50 J/cm²

@Temperature 23.0 °C
 26.2 ft-lb/in²

@Temperature 73.4 °F
 V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 70.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 38.9 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
75.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 41.7 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 70.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 38.9 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
75.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 41.7 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
Thermal Conductivity 0.200 W/m-K
1.39 BTU-in/hr-ft²-°F
ISO 8302
Deflection Temperature at 0.46 MPa (66 psi) 126 °C
259 °F
Edgew 120*10*4 sp=100mm; ISO 75/Be
Deflection Temperature at 1.8 MPa (264 psi) 113 °C
235 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
Vicat Softening Point 134 °C
273 °F
Rate B/50; ISO 306
135 °C
275 °F
Rate B/120; ISO 306
UL RTI, Electrical 100 °C
212 °F
UL 746B
UL RTI, Mechanical with Impact 100 °C
212 °F
UL 746B
UL RTI, Mechanical without Impact 100 °C
212 °F
UL 746B
Flammability, UL94 V-1

@Thickness 1.00 mm
 V-1

@Thickness 0.0394 in
 UL 94
V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
 UL 94
Oxygen Index 38 %
38 %
LOI; ISO 4589
Glow Wire Test 825 °C

@Thickness 2.00 mm
 1520 °F

@Thickness 0.0787 in
 Glow Wire Ignitability Temperature; IEC 60695-2-13
825 °C

@Thickness 1.00 mm
 1520 °F

@Thickness 0.0394 in
 Glow Wire Ignitability Temperature; IEC 60695-2-13
960 °C

@Thickness 1.50 mm
 1760 °F

@Thickness 0.0591 in
 Glow Wire Flammability Index; IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
ROA; IEC 60093
Dielectric Constant 2.7

@Frequency 1.00e+6 Hz
 2.7

@Frequency 1.00e+6 Hz
 IEC 60250
2.7

@Frequency 50.0 - 60.0 Hz
 2.7

@Frequency 50.0 - 60.0 Hz
 IEC 60250
Dielectric Strength 18.0 kV/mm

@Thickness 3.20 mm
 457 kV/in

@Thickness 0.126 in
 in oil; IEC 60243-1
25.0 kV/mm

@Thickness 1.60 mm
 635 kV/in

@Thickness 0.0630 in
 in oil; IEC 60243-1
35.0 kV/mm

@Thickness 0.800 mm
 889 kV/in

@Thickness 0.0315 in
 in oil; IEC 60243-1
Dissipation Factor 0.0010

@Frequency 50.0 - 60.0 Hz
 0.0010

@Frequency 50.0 - 60.0 Hz
 IEC 60250
0.010

@Frequency 1.00e+6 Hz
 0.010

@Frequency 1.00e+6 Hz
 IEC 60250
Comparative Tracking Index 175 - 250 V
175 - 250 V
PLC code 3; UL 746A
225 V
225 V
IEC 60112
Hot Wire Ignition, HWI 30 - 60 sec
30 - 60 sec
PLC code 2; UL 746A
High Amp Arc Ignition, HAI >= 120 arcs
>= 120 arcs
surface, PLC code 0; UL 746A
Descriptive Properties Value Comments
Ball Pressure Test, 125°C +/- 2°C PASSES
IEC 60695-10-2