SABIC Innovative Plastics Cycoloy® CE8510 PC+ABS (Asia Pacific)

Category	Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	Cycoloy®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics Cycoloy® CE8510 PC+ABS (Asia Pacific).pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Extrusion grade PC/ABS. Low viscosity, high impact and ductility.This data was supplied by SABIC-IP for the Asia Pacific region.

Physical Properties	Metric	English	Comments
Specific Gravity	1.14 g/cc	1.14 g/cc	ASTM D 792
Density	1.14 g/cc	0.0412 lb/in³	ISO 1183
Moisture Absorption at Equilibrium	0.10 %	0.10 %	23°C / 50% RH; ISO 62
Water Absorption at Saturation	0.10 % @Temperature 23.0 °C	0.10 % @Temperature 73.4 °F	ISO 62
Linear Mold Shrinkage, Flow	0.0050 - 0.0070 cm/cm @Thickness 3.20 mm	0.0050 - 0.0070 in/in @Thickness 0.126 in	SABIC Method
Linear Mold Shrinkage, Transverse	0.0050 - 0.0070 cm/cm @Thickness 3.20 mm	0.0050 - 0.0070 in/in @Thickness 0.126 in	SABIC Method
Melt Flow	8.5 g/10 min @Load 5.00 kg, Temperature 260 °C	8.5 g/10 min @Load 11.0 lb, Temperature 500 °F	ASTM D 1238
	10 g/10 min @Load 5.00 kg, Temperature 265 °C	10 g/10 min @Load 11.0 lb, Temperature 509 °F	[cm^3/10 min] Melt Volume Rate; ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	45.0 MPa	6530 psi	50 mm/min; ISO 527
	56.0 MPa	8120 psi	Type I, 50 mm/min; ASTM D 638
Tensile Strength, Yield	50.0 MPa	7250 psi	50 mm/min; ISO 527
	57.0 MPa	8270 psi	Type I, 50 mm/min; ASTM D 638
Elongation at Break	>= 50 %	>= 50 %	50 mm/min; ISO 527
	125 %	125 %	Type I, 50 mm/min; ASTM D 638
Elongation at Yield	4.0 %	4.0 %	50 mm/min; ISO 527
	4.9 %	4.9 %	Type I, 50 mm/min; ASTM D 638
Tensile Modulus	2.17 GPa	315 ksi	5 mm/min; ASTM D 638
	2.25 GPa	326 ksi	1 mm/min; ISO 527
Flexural Yield Strength	85.0 MPa	12300 psi	1.3 mm/min, 50 mm span; ASTM D 790
	85.0 MPa	12300 psi	2 mm/min; ISO 178
Flexural Modulus	2.30 GPa	334 ksi	2 mm/min; ISO 178
	2.35 GPa	341 ksi	1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched	5.30 J/cm @Temperature -30.0 °C	9.93 ft-lb/in @Temperature -22.0 °F	ASTM D 256
	6.50 J/cm @Temperature 23.0 °C	12.2 ft-lb/in @Temperature 73.4 °F	ASTM D 256
Izod Impact, Notched (ISO)	35.0 kJ/m² @Temperature -30.0 °C	16.7 ft-lb/in² @Temperature -22.0 °F	80103; ISO 180/1A
	50.0 kJ/m² @Temperature 23.0 °C	23.8 ft-lb/in² @Temperature 73.4 °F	80103; ISO 180/1A
Charpy Impact, Notched	3.50 J/cm² @Temperature -30.0 °C	16.7 ft-lb/in² @Temperature -22.0 °F	V-notch Edgew 80103 sp=62mm; ISO 179/1eA
	5.00 J/cm² @Temperature 23.0 °C	23.8 ft-lb/in² @Temperature 73.4 °F	V-notch Edgew 80103 sp=62mm; ISO 179/1eA
Impact Test	60.0 J @Temperature 23.0 °C	44.3 ft-lb @Temperature 73.4 °F	Instrumented Impact Total Energy; ASTM D 3763

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	72.0 µm/m-°C @Temperature -40.0 - 40.0 °C	40.0 µin/in-°F @Temperature -40.0 - 104 °F	ASTM E 831
	72.0 µm/m-°C @Temperature -40.0 - 40.0 °C	40.0 µin/in-°F @Temperature -40.0 - 104 °F	ISO 11359-2
CTE, linear, Transverse to Flow	80.0 µm/m-°C @Temperature -40.0 - 40.0 °C	44.4 µin/in-°F @Temperature -40.0 - 104 °F	ASTM E 831
	80.0 µm/m-°C @Temperature -40.0 - 40.0 °C	44.4 µin/in-°F @Temperature -40.0 - 104 °F	ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi)	124 °C @Thickness 3.20 mm	255 °F @Thickness 0.126 in	unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi)	120 °C	248 °F	Flatw 80104 sp=64mm; ISO 75/Af
	107 °C @Thickness 3.20 mm	225 °F @Thickness 0.126 in	unannealed; ASTM D 648
Vicat Softening Point	118 °C	244 °F	Rate B/50; ASTM D 1525
	118 °C	244 °F	Rate B/50; ISO 306
	122 °C	252 °F	Rate B/120; ISO 306

Descriptive Properties	Value	Comments
Ball Pressure Test, 75°C +/- 2°C	PASSES	IEC 60695-10-2