- Thermoplastic
- Ethylene Methyl Acrylate
- Ethylene-Methyl Acrylate Copolymer, Molding Grade
- DuPont Elvaloy® 1820 AC Ethylene and 20% Methyl Acrylate Copolymer
DuPont Elvaloy® 1820 AC Ethylene and 20% Methyl Acrylate Copolymer
| Category | Polymer , Film , Thermoplastic , Ethylene Methyl Acrylate , Ethylene-Methyl Acrylate Copolymer, Molding Grade |
| Manufacturer | DuPont Packaging and Industrial Polymers |
| Trade Name | Elvaloy® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Elvaloy® 1820 AC Ethylene and 20% Methyl Acrylate Copolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Elvaloy® 1820 AC is intended for film coextrusion, compounding and injection molding. Due to its high melt flow rate, it also can be used in extrusion coating/lamination. Elvaloy® 1820 AC has good adhesion to carious substrates (OPA, OPP, paperboard, etc.), gives excellent sealing properties and has high filler acceptance.Elvaloy® 1820 AC is easily processed on standard equipment used for low density polyethylene.Information provided by DuPont.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.942 g/cc | 0.0340 lb/in³ | ASTM D792 - ISO 1183 |
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
8.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 - ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 87 | 87 | ASTM D2240 - ISO 868 |
| Hardness, Shore D | 28 | 28 | ASTM D2240 - ISO 868 |
| Tensile Strength at Break | 11.0 MPa | 1600 psi | 500 mm/min; ASTM D638 - ISO 527-2 |
| Elongation at Break | 780 % | 780 % | 500 mm/min; ASTM D638 - ISO 527-2 |
| Tensile Modulus | 0.0350 GPa | 5.08 ksi | 1 mm/min; ASTM D638 - ISO 527-2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 92.0 °C | 198 °F | By DSC; ASTM D3418 - ISO 3146 |
| Vicat Softening Point | 54.0 °C | 129 °F | A<sub>50</sub> (10N); ASTM D1525 - ISO 306 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 150 °C | 302 °F | Extrusion lamination and extrusion coating |
| 150 °C | 302 °F | Cast film | |
| 150 °C | 302 °F | Blown film | |
| Middle Barrel Temperature | 160 °C | 320 °F | Blown film |
| 210 °C | 410 °F | Cast film | |
| 220 °C | 428 °F | Extrusion lamination | |
| Front Barrel Temperature | 170 °C | 338 °F | Blown film |
| 250 °C | 482 °F | Cast film | |
| 290 °C | 554 °F | Extrusion lamination | |
| Adapter Temperature | 180 °C | 356 °F | Blown film |
| 250 °C | 482 °F | Cast Film | |
| 290 °C | 554 °F | Extrusion lamination | |
| Die Temperature | 180 °C | 356 °F | Blown film |
| 250 °C | 482 °F | Cast film | |
| 290 °C | 554 °F | Extrusion lamination |
| Descriptive Properties | Value | Comments |
|---|---|---|
| MA-Content | 20 wt.% | DuPont Method |
Users viewing this material also viewed the following:
- Fiberfil® J-68/30/E Polypropylene Copolymer, 30% Glass Fiber Reinforced, Chemically coupled
- Gouda Vuurvast LP 80 A Dense Refractory Brick
- Polyplastics Duranex® CN7000 Polybutylene Terephthalate (PBT), Standard, FR, UL approved regrind 50%
- A. Schulman POLYBATCH™ Blue LL40299U/3 Concentrate Based In LLDPE
- A. Schulman POLYPUR™ FPU 1380 Thermoplastic Polyurethane Compound
- Zircar Zirconia YF-100 Yttria Felt Insulation
- Tra-Con Tra-Bond F156 Optically Opaque Epoxy Adhesive
- ExxonMobil Mobil Rarus 826
- CENTROPLAST CENTROPEEK Polyetheretherketone
- Asia International Enterprise (Hong Kong) ST60G3 Nylon 66, 15% Filled
Copyright © lookpolymers.com All Rights Reserved