Polymer Resources PC/ABS-G20 General Purpose PC/ABS Alloy, 20% Glass Filled
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Glass Fiber Filled , Polycarbonate (PC) |
| Manufacturer | Polymer Resources, LTD |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polymer Resources PC/ABS-G20 General Purpose PC/ABS Alloy, 20% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PC/ABS Alloy, General Purpose, 20% Glass FilledProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.25 g/cc | 1.25 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0020 - 0.0050 cm/cm | 0.0020 - 0.0050 in/in | ASTM D955 |
| Melt Flow | 2.0 - 12 g/10 min @Load 5.00 kg, Temperature 250 °C |
2.0 - 12 g/10 min @Load 11.0 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 72.4 MPa | 10500 psi | ASTM D638 |
| Tensile Strength, Yield | 72.4 MPa | 10500 psi | ASTM D638 |
| Flexural Strength | 121 MPa | 17500 psi | ASTM D790 |
| Flexural Modulus | 5.17 GPa | 750 ksi | ASTM D790 |
| Izod Impact, Notched | 0.747 J/cm @Temperature 22.8 °C |
1.40 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 127 °C | 260 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 118 °C | 245 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0626 in |
|
| HB @Thickness 3.17 mm |
HB @Thickness 0.125 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 249 - 288 °C | 480 - 550 °F | |
| Middle Barrel Temperature | 254 - 293 °C | 490 - 560 °F | |
| Front Barrel Temperature | 260 - 302 °C | 500 - 575 °F | |
| Melt Temperature | 271 - 299 °C | 520 - 570 °F | |
| Mold Temperature | 71.1 - 93.3 °C | 160 - 200 °F | |
| Drying Temperature | 79.4 - 85.0 °C | 175 - 185 °F | |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Vent | 0.0015 |
Users viewing this material also viewed the following:
- ExxonMobil Escorene® UL-7740 EVA Copolymer, Adhesive and Sealant Grade (discontinued **)
- Flint Hills P5M6K-048 Random Copolymer Polypropylene
- Indium Corp. Standard ITO Indium Tin Oxide
- Karina E 650D35/1-C Ivory PVC Compound
- Gromax BTE30-FN00N1 Nylon 6 (Conditioned)
- Fainplast Compounds CTS 55/1 Flexible PVC, Extrusion Modified with Rubber
- IRPC Polimaxx Porene AN520 Acrylonitrile Butadiene Styrene
- Fainplast Compounds PM 92 Flexible PVC, Extrusion
Copyright © lookpolymers.com All Rights Reserved