- RheTech Products FT4802-691UV Thermoplastic Polyolefin, UV Stabilized, RJ3 Dark Grey Green
RheTech Products FT4802-691UV Thermoplastic Polyolefin, UV Stabilized, RJ3 Dark Grey Green
| Category | Polymer , Thermoplastic , Polyolefin |
| Manufacturer | RheTech Products |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | RheTech Products FT4802-691UV Thermoplastic Polyolefin, UV Stabilized, RJ3 Dark Grey Green.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Bodyside moldings and claddingsFacia and bumper coversExterior componentsInjection molding conditions reported in table.Information provided by RheTech Products.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.01 g/cc | 1.01 g/cc | 23/23°C; ASTM D792 |
| Filler Content | 16 % | 16 % | ASTM D5630 |
| Linear Mold Shrinkage | 0.0095 cm/cm | 0.0095 in/in | ASTM D955 |
| Melt Flow | 15 g/10 min @Load 2.16 kg, Temperature 230 °C |
15 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 64 | 64 | ASTM D2240 |
| Tensile Strength at Break | 17.9 MPa | 2600 psi | 2 in/min; ASTM D638 |
| Flexural Modulus | 1.24 GPa | 180 ksi | Tangent; ASTM D790 |
| Izod Impact, Notched | 8.01 J/cm @Temperature 23.0 °C |
15.0 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Gardner Impact | 15.9 J | 11.7 ft-lb | ASTM D5420 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 107 °C | 225 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 199 - 227 °C | 390 - 440 °F | |
| Middle Barrel Temperature | 204 - 232 °C | 400 - 450 °F | |
| Front Barrel Temperature | 210 - 238 °C | 410 - 460 °F | |
| Nozzle Temperature | 216 - 227 °C | 420 - 440 °F | |
| Mold Temperature | 26.7 - 48.9 °C | 80.0 - 120 °F | |
| Drying Temperature | 65.6 - 82.2 °C | 150 - 180 °F | |
| Dry Time | 1 - 2 hour | 1 - 2 hour | |
| Moisture Content | <= 0.050 % | <= 0.050 % | Recommended |
| Injection Pressure | 55.2 - 103 MPa | 8000 - 15000 psi | |
| Hold Pressure | 27.6 - 51.7 MPa | 4000 - 7500 psi | |
| Back Pressure | 0.345 - 1.03 MPa | 50.0 - 150 psi |
Users viewing this material also viewed the following:
- Radici Radilon® S CP300 (cond.) Nylon 6
- Albis Plastics Cellulose Acetate Butyrate B9024 (UVI, Odor Mask Added), 5% Plasticizer (discontinued **)
- Momentive Performance Materials TSE397 Translucent Adhesive Sealant, Semi-Flowable
- Haynes 556® alloy, 10% cold reduction, 1065°C anneal for 5 minutes
- Techmer ES HiFill® PP CO GF15 CC 15% Glass Filled
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber
- Loctite® 4014 Cyanoacrylate Adhesive
- ExxonMobil NTX™ NTX 095 Super Strength Film Resin
- SABIC Innovative Plastics LNP Verton RX93407D PA 66
Copyright © lookpolymers.com All Rights Reserved