RheTech Products E204-00 High Density Polyethylene, Natural
| Category | Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Injection Molded |
| Manufacturer | RheTech Products |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | RheTech Products E204-00 High Density Polyethylene, Natural.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Electrical housingsUnderhood componentsConsumer GoodsInjection molding conditions reported in table.Information provided by RheTech Products.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.955 g/cc | 0.955 g/cc | 23/23°C; ASTM D792 |
| Linear Mold Shrinkage | 0.020 cm/cm | 0.020 in/in | ASTM D955 |
| Melt Flow | 35 g/10 min @Load 2.16 kg, Temperature 230 °C |
35 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 58 | 58 | ASTM D2240 |
| Tensile Strength at Break | 22.8 MPa | 3300 psi | 2 in/min; ASTM D638 |
| Flexural Modulus | 0.896 GPa | 130 ksi | Tangent; ASTM D790 |
| Izod Impact, Notched | 0.427 J/cm @Temperature 23.0 °C |
0.800 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Gardner Impact | 22.6 J | 16.7 ft-lb | ASTM D5420 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 65.0 °C | 149 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 44.4 °C | 112 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 149 - 160 °C | 300 - 320 °F | |
| Middle Barrel Temperature | 154 - 171 °C | 310 - 340 °F | |
| Front Barrel Temperature | 160 - 179 °C | 320 - 355 °F | |
| Nozzle Temperature | 160 - 171 °C | 320 - 340 °F | |
| Mold Temperature | 15.6 - 26.7 °C | 60.0 - 80.0 °F | |
| Drying Temperature | 37.8 - 48.9 °C | 100 - 120 °F | |
| Dry Time | 1 - 2 hour | 1 - 2 hour | |
| Moisture Content | <= 0.050 % | <= 0.050 % | Recommended |
| Injection Pressure | 2.76 - 10.3 MPa | 400 - 1500 psi | |
| Hold Pressure | 2.07 - 8.27 MPa | 300 - 1200 psi | |
| Back Pressure | 0.345 - 1.03 MPa | 50.0 - 150 psi |
Users viewing this material also viewed the following:
- Fiberfil® J-60/15/E Polypropylene Homopolymer, 15% Glass Reinforced, Chemically coupled
- Techmer ES Luriblend® PA6/6 GF10 M/TL10 10% Glass Filled
- Wieland Porta Geo Ti PFM Alloy
- Total PS CPDS 853 Flame Retardant Polystyrene
- ChevronTexaco RPM® SAE 75W-90 Synthetic Gear Lubricant
- E-Polymers TEKALOY® S630XB Heat Resistance, Weatherability PC/PBT Alloy
- Colorite Polymers Self Frosting™ 9511SF Vinyl Compound
- 3M Scotch-Weld™ DP810NS Structural Adhesive
- Zeon Chemicals Nipol® DN508SCR Polyblend Nitrile Elastomer
Copyright © lookpolymers.com All Rights Reserved