SABIC Innovative Plastics LNP THERMOTUF PX06417 PA 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Thermotuf |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOTUF PX06417 PA 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOTUF* PX06417 is a compound based on Nylon 6 resin containing Glass Fiber. Added features of this material include: Heat Stabilized.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.46 g/cc | 0.0527 lb/in³ | ASTM D792 |
| 1.46 g/cc | 0.0527 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.640 % | 0.640 % | 50% RH, 24 hrs; ASTM D570 |
| 1.02 % | 1.02 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0017 cm/cm @Time 86400 sec |
0.0017 in/in @Time 24.0 hour |
ISO 294 |
| 0.0020 cm/cm @Time 86400 sec |
0.0020 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm @Time 86400 sec |
0.0090 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0093 cm/cm @Time 86400 sec |
0.0093 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 147 MPa | 21300 psi | ISO 527 |
| 152 MPa | 22000 psi | ASTM D638 | |
| Elongation at Break | 2.4 % | 2.4 % | ASTM D638 |
| 2.9 % | 2.9 % | ISO 527 | |
| Tensile Modulus | 11.4 GPa | 1650 ksi | 1 mm/min; ISO 527 |
| 12.82 GPa | 1859 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 228 MPa | 33100 psi | ASTM D790 |
| 243 MPa | 35200 psi | ISO 178 | |
| Flexural Modulus | 8.96 GPa | 1300 ksi | ASTM D790 |
| 11.0 GPa | 1600 ksi | ISO 178 | |
| Izod Impact, Notched | 1.49 J/cm | 2.79 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 10.89 J/cm | 20.40 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 70.0 kJ/m² | 33.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 15.0 J | 11.1 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 4.00 J | 2.95 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 25.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
14.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 25.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
14.0 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 55.9 µm/m-°C @Temperature -40.0 - 40.0 °C |
31.1 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 56.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
31.1 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C @Thickness 3.20 mm |
428 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 207 °C | 405 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 208 °C @Thickness 3.20 mm |
406 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
UL 94 by SABIC-IP |
Users viewing this material also viewed the following:
- ExxonMobil Vyram™ 9101-85 Thermoplastic Elastomer (discontinued **)
- Plenco Valite 424 Novolac Phenolic, Granular, Injection Molded (discontinued **)
- Ineos ABS Triax® KU2-3154 ABS + Polyamide Blend (Conditioned), Injection Molding Grade
- H.C. Starck Amperit® 586.1 Chromium Carbide-Nickel Chromium 80-20 (Cr3C2-NiCr)
- Multibase Multibatch® MP 52206 Anti-split
- Wieland BioPortadur Casting Alloy
- ExxonMobil Bicor™ 32MB777 OPP Film
- DuPont Performance Polymers Kalrez® 8085 Gas Deposition Compound
- 3M 927 Adhesive Transfer Tapes with Adhesive 300
- Nye Lubricants 706D (IG) Synthetic Oil
Copyright © lookpolymers.com All Rights Reserved