Sax Polymers SAXAMID 126F6 Nylon 6, 30% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | Sax Polymers |
| Trade Name | SAXAMID |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sax Polymers SAXAMID 126F6 Nylon 6, 30% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
SAXAMID 126F6 is a polyamide 6 injection-molding-grade reinforced with 30% glass fibers. Because of its high strength and stiffness this grade is often used for stressed parts. Other properties are very good processability and good surface quality.Information provided by SAX Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | ISO 1183 |
| Viscosity Test | 150 cm³/g | 150 cm³/g | H<sub>2</sub>SO<sub>4</sub>; ISO 307 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 190 MPa | 27600 psi | 5 mm/min; ISO 527-1 |
| Elongation at Break | 4.0 % | 4.0 % | 5 mm/min; ISO 527-1 |
| Tensile Modulus | 9.20 GPa | 1330 ksi | 1 mm/min; ISO 527-1 |
| Flexural Strength | 280 MPa | 40600 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 7.60 GPa | 1100 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1A |
| 13.0 kJ/m² @Temperature 23.0 °C |
6.19 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 78.0 kJ/m² @Temperature -30.0 °C |
37.1 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1U |
| 82.0 kJ/m² @Temperature 23.0 °C |
39.0 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1U | |
| Charpy Impact Unnotched | 8.00 J/cm² @Temperature -30.0 °C |
38.1 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 8.50 J/cm² @Temperature 23.0 °C |
40.4 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 1.10 J/cm² @Temperature -30.0 °C |
5.23 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 1.30 J/cm² @Temperature 23.0 °C |
6.19 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 209 °C | 408 °F | 80*10*4 s=60mm; ISO 75-1 a |
| Vicat Softening Point | 216 °C | 421 °F | B/120; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
IEC 60695-11-10 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 - 290 °C | 500 - 554 °F | |
| Mold Temperature | 70.0 - 90.0 °C | 158 - 194 °F | |
| Drying Temperature | 80.0 °C @Time 7200 - 21600 sec |
176 °F @Time 2.00 - 6.00 hour |
|
| Moisture Content | <= 0.20 % | <= 0.20 % |
Users viewing this material also viewed the following:
- Ovation Polymers UTTAP QU HT530 GF Nylon, 30% Glass Reinforced
- NIZHNEKAMSKNEFTEKHIM PE 4142L (424F5) High Density Polyethylene
- SABIC Innovative Plastics Lexan® BFL2000U PC (Asia Pacific)
- Sylvin Technologies 8960-90 Natural PVC Extrusion Compound
- Covestro Bayblend® T45 PG Polycarbonate + ABS
- ConocoPhillips HD Fleet™ 40 Engine Oil
- EMS-Griltech Grilon® M 369 White Nylon 6 Fiber
- Braskem FPT300F Homopolymer Polypropylene
- Zotefoams Plastazote® LD34 Low Density Polyethylene Foam
- Lushan EV1050G2 EVA Film for Encapsulating Solar modules, High Transmittance
Copyright © lookpolymers.com All Rights Reserved