Resinlab® EP1056LC Urethane Modified Epoxy Adhesive

Category Polymer , Adhesive , Thermoset , Epoxy , Epoxy Adhesive
Manufacturer Resinlab®
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Resinlab® EP1056LC Urethane Modified Epoxy Adhesive.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Resinlab™ EP1056LC is a two part urethane modified epoxy adhesive designed to give good adhesion to metals and hard to bond surfaces such as PVC. It is thixotropic to provide good gap filling ability and prevent running and sagging during cure. It has very good resistance to water, acids and bases and most organic solvents. It was especially formulated to a 2A:1B mix ratio for use in automatic mixing equipment and dispensers with static mixers. EP1056LC will reach handle cure at room temperature within 8 – 16 hours. Cure time can be accelerated by the application of heat. Times and temperatures from 2 hours at 65°C to 10 minutes at 100°C are typical for most applications. Time to heat substrate must be taken into account. Cooler temperatures will also extend work time and increase cure times.Information Provided by Resinlab L.L.C., an Ellsworth Adhesives Company.
Physical Properties Metric English Comments
Specific Gravity 0.970 g/cc
0.970 g/cc
Part B; TM R050-16
1.10 g/cc
1.10 g/cc
Mixed; TM R050-16
1.17 g/cc
1.17 g/cc
Part A; TM R050-16
Water Absorption 0.12 %

@Time 86400 sec
0.12 %

@Time 24.0 hour
TM R050-35
Viscosity 4000 cP
4000 cP
Part B, RVT, #4, 2.5 rpm; TM R050-12
165000 cP
165000 cP
Mixed; TM R050-12
325000 cP
325000 cP
Part A, RVT, #7, 2.5 rpm; TM R050-12
Mechanical Properties Metric English Comments
Hardness, Shore D 80
80
TM R050-17
Tensile Strength at Break 34.5 MPa
5000 psi
TM R050-36
Tensile Strength, Ultimate 34.5 MPa
5000 psi
TM R050-36
Tensile Strength, Yield 10.3 MPa
1500 psi
TM R050-36
Elongation at Break 2.0 - 3.0 %
2.0 - 3.0 %
TM R050-36
Tensile Modulus 2.41 GPa
350 ksi
TM R050-36
Compressive Yield Strength 58.6 MPa
8500 psi
TM R050-38
Compressive Strength 114 MPa
16500 psi
Break; TM R050-38
117 MPa
17000 psi
Ultimate; TM R050-38
Compressive Modulus 2.34 GPa
340 ksi
TM R050-38
Adhesive Bond Strength 24.1 MPa
3500 psi
Lap shear; 2024 T3 Al Abraded / MEK Wipe; TM R050-37
Thermal Properties Metric English Comments
CTE, linear 55.0 µm/m-°C
30.6 µin/in-°F
Thermal Conductivity 0.160 W/m-K
1.11 BTU-in/hr-ft²-°F
Maximum Service Temperature, Air 150 °C
302 °F
Minimum Service Temperature, Air -40.0 °C
-40.0 °F
Glass Transition Temp, Tg 50.0 °C
122 °F
TM R050-25
Electrical Properties Metric English Comments
Volume Resistivity 8.00e+14 ohm-cm
8.00e+14 ohm-cm
Dielectric Constant 4.5

@Frequency 100 Hz,
Temperature 25.0 °C
4.5

@Frequency 100 Hz,
Temperature 77.0 °F
Dielectric Strength 16.1 kV/mm
410 kV/in
Processing Properties Metric English Comments
Cure Time 120 min

@Temperature 65.0 °C
2.00 hour

@Temperature 149 °F
1440 - 4320 min

@Temperature 25.0 °C
24.0 - 72.0 hour

@Temperature 77.0 °F
Pot Life 30 min
30 min
Mass: 50g; TM R050-19
Descriptive Properties Value Comments
Color Black
Mix Ratio 2:1
Volume
245:100
Weight