BASF Ultramid® B3WG5 BK 00654 PA6 25% Glass Filled BK (Dry)

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled
Manufacturer	BASF
Trade Name	Ultramid®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BASF Ultramid® B3WG5 BK 00654 PA6 25% Glass Filled BK (Dry).pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Description: 25% glass-fiber reinforced and heat aging resistant injection-molding grade, for instance, for fan impeller glass-fiber reinforced injection-molding grade for industrial articles and electrical insulating parts.Information provided by BASF

Physical Properties	Metric	English	Comments
Bulk Density	0.500 - 0.800 g/cc	0.0181 - 0.0289 lb/in³
Density	1.32 g/cc	0.0477 lb/in³	ISO 1183
Water Absorption	6.8 - 7.4 %	6.8 - 7.4 %	Saturation; ISO 62
Moisture Absorption at Equilibrium	2.1 - 2.5 %	2.1 - 2.5 %	23°C; 50% RH; ISO 62
Viscosity Measurement	140	140	ISO 307
Linear Mold Shrinkage	0.0035 cm/cm	0.0035 in/in	restricted
Melt Flow	72.6 g/10 min @Load 5.00 kg, Temperature 275 °C	72.6 g/10 min @Load 11.0 lb, Temperature 527 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	160 MPa	23200 psi	50 mm/min; ISO 527-1/-2
Elongation at Yield	3.5 %	3.5 %	50 mm/min; ISO 527-1/-2
Modulus of Elasticity	8.00 GPa	1160 ksi	ISO 527-1/-2
Flexural Strength	220 MPa	31900 psi	at max force; ISO 178
Flexural Modulus	7.40 GPa	1070 ksi	ISO 178
Izod Impact, Notched (ISO)	12.0 kJ/m² @Temperature 23.0 °C	5.71 ft-lb/in² @Temperature 73.4 °F	ISO 180/A
Charpy Impact Unnotched	7.50 J/cm² @Temperature -30.0 °C	35.7 ft-lb/in² @Temperature -22.0 °F	ISO 179/1eU
	8.00 J/cm² @Temperature 23.0 °C	38.1 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eU
Charpy Impact, Notched	1.00 J/cm² @Temperature -30.0 °C	4.76 ft-lb/in² @Temperature -22.0 °F	ISO 179/1eA
	1.20 J/cm² @Temperature 23.0 °C	5.71 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eA

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	20.0 - 25.0 µm/m-°C @Temperature 23.0 - 80.0 °C	11.1 - 13.9 µin/in-°F @Temperature 73.4 - 176 °F	DIN 11359-1/-2
CTE, linear, Transverse to Flow	60.0 - 70.0 µm/m-°C @Temperature 23.0 - 80.0 °C	33.3 - 38.9 µin/in-°F @Temperature 73.4 - 176 °F	DIN 11359-1/-2
Thermal Conductivity	0.350 W/m-K	2.43 BTU-in/hr-ft²-°F	DIN 52612
Melting Point	220 °C	428 °F	DIN 53765
Maximum Service Temperature, Air	145 °C	293 °F	for 50% loss of tensile strength after 20000hr
	175 °C	347 °F	for 50% loss of tensile strength after 5000hr
	200 °C	392 °F
Deflection Temperature at 0.46 MPa (66 psi)	220 °C	428 °F	ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)	210 °C	410 °F	ISO 75-1/-2
Decomposition Temperature	>= 300 °C	>= 572 °F
Flammability, UL94	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+13 ohm-cm	1.00e+13 ohm-cm	IEC 60093
Dielectric Constant	3.8 @Frequency 1.00 Hz	3.8 @Frequency 1.00 Hz	IEC 60250
Dissipation Factor	0.025 @Frequency 1.00e+6 Hz	0.025 @Frequency 1.00e+6 Hz	IEC 60250
Comparative Tracking Index	450 V	450 V	Test solution A; IEC 60112

Processing Properties	Metric	English	Comments
Processing Temperature	80.0 °C	176 °F	Hopper Throat
Zone 1	260 °C	500 °F	Feed Zone
Zone 2	270 °C	518 °F	Compression
Zone 3	280 °C	536 °F	Metering-zone
Zone 4	280 °C	536 °F	Nozzle
Melt Temperature	270 - 290 °C	518 - 554 °F	Injection-molding/Extrusion
	280 °C	536 °F	Optimal
Mold Temperature	80.0 °C	176 °F	Optimal
	80.0 - 90.0 °C	176 - 194 °F	Injection-molding
Drying Temperature	80.0 °C	176 °F
Dry Time	4 hour	4 hour
Moisture Content	0.030 - 0.060 %	0.030 - 0.060 %	Optimal
	<= 0.15 %	<= 0.15 %

Descriptive Properties	Value	Comments
Color	BK 00564
Commercial Status	Europe
Ignition Temperature	>400°C	ASTM D129
Peripheral screw speed	< 0.3 m/s