Polykemi AB SCANMID 6 B11^ F30 FR5 Nylon 6, Glass Fiber Reinforced, Flame Retardant

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled , Nylon 6, Glass Fiber Filled, Flame Retardant
Manufacturer Polykemi AB
Trade Name SCANMID 6
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polykemi AB SCANMID 6 B11^ F30 FR5 Nylon 6, Glass Fiber Reinforced, Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Polykemi AB
Physical Properties Metric English Comments
Density 1.52 g/cc
0.0549 lb/in³
ISO 1183
Filler Content 30 %
30 %
±2%; Polykemi
Linear Mold Shrinkage 0.0030 cm/cm
0.0030 in/in
With Flow; ISO 2577
0.0090 cm/cm
0.0090 in/in
Across Flow; ISO 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break <= 140 MPa
<= 20300 psi
ISO/R527
Elongation at Break 9.0 %
9.0 %
ISO/R527
Flexural Strength <= 225 MPa
<= 32600 psi
ISO 178
Flexural Modulus 9.00 GPa

@Temperature 23.0 °C
 1310 ksi

@Temperature 73.4 °F
 ISO 178
Charpy Impact, Notched 0.600 J/cm²

@Temperature -20.0 °C
 2.86 ft-lb/in²

@Temperature -4.00 °F
 ISO 179
1.00 J/cm²

@Temperature 23.0 °C
 4.76 ft-lb/in²

@Temperature 73.4 °F
 ISO 179
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 195 °C
383 °F
120°C/h; ISO 75/1
Vicat Softening Point 205 °C

@Load 5.001 kg
 401 °F

@Load 11.03 lb
 50°C/h; ISO 306
Flammability, UL94 V-0

@Thickness 3.20 mm
 V-0

@Thickness 0.126 in