- Ravago Manufacturing Americas Hylon® N1033L Nylon 6/6 (DAM) (discontinued **)
Ravago Manufacturing Americas Hylon® N1033L Nylon 6/6 (DAM) (discontinued **)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ravago Manufacturing Americas Hylon® N1033L Nylon 6/6 (DAM)
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Ravago.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.38 g/cc | 0.0499 lb/in³ | ASTM D792 |
| Water Absorption | 0.70 % | 0.70 % | 24 hrs; ASTM D570 |
| Linear Mold Shrinkage | 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in | 0.125 in; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 98 | 98 | ASTM D785 |
| Tensile Strength at Break | 193 MPa | 28000 psi | ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D638 |
| Flexural Strength | 262 MPa | 38000 psi | ASTM D790 |
| Flexural Modulus | 9.31 GPa | 1350 ksi | ASTM D790 |
| Izod Impact, Notched | 1.17 J/cm | 2.20 ft-lb/in | 73°F; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 23.4 µm/m-°C @Temperature 20.0 °C |
13.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 249 °C | 480 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB | 0.0590 in, BK |
| HB | HB | 0.0590 in, NC | |
| HB | HB | 0.118 in, BK | |
| HB | HB | 0.118 in, NC | |
| HB | HB | 0.0295 in, NC |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Dielectric Strength | 20.5 kV/mm | 520 kV/in | ASTM D149 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 282 - 299 °C | 540 - 570 °F | |
| Mold Temperature | 65.6 - 98.9 °C | 150 - 210 °F | |
| Drying Temperature | 73.9 °C | 165 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | |
| Moisture Content | 0.20 % | 0.20 % | |
| Back Pressure | 0.138 - 0.414 MPa | 20.0 - 60.0 psi | |
| Screw Speed | 40 - 120 rpm | 40 - 120 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Holding Pressure | 750 to 1400 psi | |
| Injection Rate | Fast |
Users viewing this material also viewed the following:
- Abatron AboCast 8-7/Abocure 8-7 Epoxy (discontinued **)
- DuPont Performance Polymers Zytel® 73G45 BK263 Nylon 6 (Unverified Data**)
- Shandong Dongyue Polymer DF-204 PTFE Fine Powder
- Teknor Apex Uniprene® UN-2028A UMB Thermoplastic Elastomer
- Plenco 4527 Phenolic, Granular, Transfer Molded
- ExxonMobil 23 Mobilux EP
- CP-Polymer-Technik Wellamid® 6600/58 HWCP Nylon 66, Impact Modified Until -40°C, Heat Stabilized, Dry
- Plaskolite West Optix® CA-1000 I Clear High Impact Acrylic Resin
- Ascend Performance Materials Vydyne® 50BWFS Nylon 66, Dry as Molded
Copyright © lookpolymers.com All Rights Reserved