Braskem H 604 Blow Molding Polypropylene
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Blow Molding Grade |
| Manufacturer | Braskem |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Braskem H 604 Blow Molding Polypropylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Transparent bottles for mineral water, cosmetic, health care and cleaning products. Information provided by Braskem
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.905 g/cc | 0.0327 lb/in³ | ASTM D792A |
| Melt Flow | 1.5 g/10 min @Load 2.16 kg, Temperature 230 °C |
1.5 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238L |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 85 | 85 | ASTM D785 |
| Tensile Strength, Yield | 38.0 MPa | 5510 psi | ASTM D638 |
| Elongation at Yield | 10 % | 10 % | ASTM D638 |
| Flexural Modulus | 1.73 GPa | 251 ksi | ASTM D790 |
| Izod Impact, Notched | 0.560 J/cm @Temperature 23.0 °C |
1.05 ft-lb/in @Temperature 73.4 °F |
ASTM D256A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 103 °C | 217 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ASTM D648 |
| Vicat Softening Point | 149 °C | 300 °F | -1kg; ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 90 % | 90 % | transparent; thickness not quantified |
Users viewing this material also viewed the following:
- PolyOne Maxxam™ FR PP FR 7B31 Polypropylene, Unspecified (PP, Unspecified)
- Ineos T20N-00 Polypropylene Impact Copolymer
- Saint-Gobain Fluoroloy® A01 High Performance Seal Material
- Teknor Apex Telcar® TL-2545A Thermoplastic Elastomer
- A. Schulman COMTUF® 5011 10% Glass Fiber Reinforced Polycarbonate
- A. Schulman POLYBATCH™ U-0294-L Blowing Agent Concentrate Based In PE
- Elektro-Isola G-Etronax B Phenolic, Glass Fabric Reinforcement, Dark Brown, Tubes
- DSM Akulon® Ultraflow K-FHGM35 PA6-(GF+MD)40
Copyright © lookpolymers.com All Rights Reserved