Premix Thermoplastics PRE-ELEC® ESD 5350 Static Dissipative Thermoplastic Compound

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Molded
Manufacturer Premix Thermoplastics Inc.
Trade Name PRE-ELEC®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Premix Thermoplastics PRE-ELEC® ESD 5350 Static Dissipative Thermoplastic Compound.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PRE-ELEC® ESD 5350 is a static dissipative thermoplastic compounds based on polypropylene homopolymer. The dissipative property is permanent and built into the polymer chain. Surface resistance values of 1010 O with PRE-ELEC® (EOS/ESD S11.11-1993, IEC 61340-5-1) can be achieved. The products made out of these PRE-ELEC® ESD products are washable, reusable and recyclable. The grade is designed for injection molding of transparent parts. In addition, PRE-ELEC® ESD 5350 can be used in clean applications with extremely low amount of extractable ions. The melt flow property of PRE-ELEC® ESD 5350 is tailored to fit the requirements of injection molding. PRE-ELEC® ESD 5350 is RoHS compliant.Applications: Bins and other injection molded parts, where permanent ESD protection and high cleanliness are required. The product can be used mainly in electronics packaging, but in many other application areas as well.Processing: PRE-ELEC® ESD 5350 compound can be processed in normal processing conditions as with polypropylene.Test Specimen: 10[mm] wide moulded rodInformation from Premix OY
Physical Properties Metric English Comments
Density 0.920 g/cc
0.0332 lb/in³
Thickness 102 microns
4.00 mil
Linear Mold Shrinkage 0.016 cm/cm
0.016 in/in
ISO 294-4
Melt Flow 8.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
8.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength 16.0 MPa
2320 psi
ISO 527
Tensile Strength, Yield 30.0 MPa
4350 psi
ISO 527
Elongation at Break 200 %
200 %
ISO 527
Elongation at Yield 15 %
15 %
ISO 527
Flexural Modulus 1.50 GPa
218 ksi
ISO 178
Izod Impact, Notched (ISO) 4.00 kJ/m²

@Thickness 4.00 mm,
Temperature 23.0 °C
1.90 ft-lb/in²

@Thickness 0.157 in,
Temperature 73.4 °F
ISO 180
Izod Impact, Unnotched (ISO) NB

@Thickness 4.00 mm,
Temperature 23.0 °C
NB

@Thickness 0.157 in,
Temperature 73.4 °F
ISO 180
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 90.0 °C
194 °F
75/Method Bf
Deflection Temperature at 1.8 MPa (264 psi) 55.0 °C
131 °F
75/Method Af
Optical Properties Metric English Comments
Transmission, Visible 90 %
90 %
transparent; thickness not quantified
Electrical Properties Metric English Comments
Surface Resistance 1.00e+10 - 1.00e+11 ohm
1.00e+10 - 1.00e+11 ohm
ISO IEC 61340-5-1
Static Decay 2.0 sec
2.0 sec
ISO IEC 61340-5-1
Processing Properties Metric English Comments
Zone 1 180 °C
356 °F
Cylinder
210 °C
410 °F
Die
Zone 2 190 °C
374 °F
Cylinder
210 °C
410 °F
Die
Zone 3 200 °C
392 °F
Die
200 °C
392 °F
Cylinder
Zone 4 210 °C
410 °F
Die
210 °C
410 °F
Cylinder
Zone 5 210 °C
410 °F
Die
210 °C
410 °F
Cylinder
Melt Temperature 190 - 210 °C
374 - 410 °F
Mold Temperature 30.0 - 40.0 °C
86.0 - 104 °F
Roll Temperature 40.0 °C
104 °F
2nd Roll
40.0 °C
104 °F
3rd Roll
50.0 °C
122 °F
1st Roll
Drying Temperature 60.0 - 80.0 °C
140 - 176 °F
Pre-drying in a dehumidifier
Dry Time 2 - 4 hour
2 - 4 hour
Injection Pressure 60.0 - 80.0 MPa
8700 - 11600 psi
Shelf Life 12.0 Month
12.0 Month
Normal Storing Conditions
Descriptive Properties Value Comments
Injection Speed Moderate