Polyram PlusTek RA303G7 Nylon 6.6, 35% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Glass Fiber Filled |
| Manufacturer | Polyram |
| Trade Name | PlusTek |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram PlusTek RA303G7 Nylon 6.6, 35% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
35% Glass fiber reinforced, heat stabilized and hydrolysis resistant polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | DIN 53479 |
| Water Absorption | 5.6 % | 5.6 % | DIN 53495 |
| Moisture Absorption at Equilibrium | 1.7 % | 1.7 % | 50%RH; DIN 53714 |
| Linear Mold Shrinkage | 0.0030 - 0.0040 cm/cm | 0.0030 - 0.0040 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 122 | 122 | ASTM-D785 |
| Tensile Strength, Yield | 190 MPa | 27600 psi | ASTM-D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM-D638 |
| Flexural Strength | 300 MPa | 43500 psi | ASTM D790 |
| Flexural Modulus | 8.20 GPa | 1190 ksi | ASTM-D790 |
| Izod Impact, Notched | 1.20 J/cm @Temperature 23.0 °C |
2.25 ft-lb/in @Temperature 73.4 °F |
ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 256 °C | 493 °F | |
| Maximum Service Temperature, Air | 110 °C | 230 °F | Continuous Use |
| >= 200 °C | >= 392 °F | Short peaks operation | |
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | DIN 53461 |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | DIN 53461 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | DIN 53482 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | DIN 53482 |
| Dielectric Constant | 3.7 @Frequency 1e+6 Hz |
3.7 @Frequency 1e+6 Hz |
VDE 0303/4 |
| Dielectric Strength | 90.0 kV/mm | 2290 kV/in | VDE 0303/4 |
Users viewing this material also viewed the following:
- Polymax® Maxelast® P3935T TPE, PP Overmold or Standalone use
- Solvay Specialty Polymers KetaSpire® KT-820P Polyetheretherketone (PEEK) (Unverified Data**)
- Fainplast Compounds RK 320 Rigid PVC, Extrusion Lead Free
- Momentive Performance Materials Siloprenâ„¢ LSR 2651 Liquid Silicone Rubber - Non Post Cure / Low Compression Set
- SABIC Innovative Plastics LNP Thermocomp AF002L ABS (Asia Pacific)
- Sibur MPP 15-06V Frost Resistant Polypropylene
- Techmer ES HiFill® HDPE GF15 15% Glass Filled
- A. Schulman ComAlloy® E-14756 Flame Retardant Easy Flow Polycarbonate Alloy
- Braskem LD5000A LDPE Blow Molding Polyethylene
- Axiall 7540 Moldings & Extrusions Flexible PVC
Copyright © lookpolymers.com All Rights Reserved