A. Schulman SCHULAMID® 6 GF15H 15% Glass Bead Reinforced, Heat Stabilized Nylon 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass Bead Filled |
| Manufacturer | A. Schulman, Inc. |
| Trade Name | SCHULAMID® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman SCHULAMID® 6 GF15H 15% Glass Bead Reinforced, Heat Stabilized Nylon 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by A. Schulman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.23 g/cc | 1.23 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.010 cm/cm @Thickness 3.175 mm |
0.010 in/in @Thickness 0.1250 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 119.89 MPa | 17388 psi | ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM D638 |
| Flexural Strength | 149.86 MPa | 21735 psi | ASTM D790 |
| Flexural Modulus | 5.1951 GPa | 753.48 ksi | ASTM D790 |
| Izod Impact, Notched | 0.534 J/cm | 1.00 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.34 J/cm | 10.0 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 211 °C | 412 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 196 °C | 385 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 270 - 295 °C | 518 - 563 °F | |
| Mold Temperature | 65.6 - 93.3 °C | 150 - 200 °F | |
| Drying Temperature | 79.4 °C | 175 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | Predrying |
Users viewing this material also viewed the following:
- Huntsman PE1041 Film Extrusion Polyethylene (discontinued **)
- IRPC Polimaxx Porene GA850 Acrylonitrile Butadiene Styrene
- Jackon JACKOCELL® R312 Expanded Polystyrene Packaging and Shape Molding
- Multibase C6-265 VAROX DBPH Dow-Corning Class VI Elastomer
- SABIC Innovative Plastics Valox® 4012G PBT (Europe-Africa-Middle East)
- Hexcel® HexWeb® CR III 1/8-5056-.0015 Corrosion Resistant Specification Grade Aluminum Honeycomb
- Eagle Brass 725 Copper Nickel Tin, 1/2 Hard
- DuPont Teijin Films Mylar® P25T Polyester Film, 50 Gauge
- Ascend Performance Materials Vydyne® 49H NT Nylon 66, Impact Modified, Conditioned
- Austin Novel Materials Texalan® 572D Polyether-based TPU
Copyright © lookpolymers.com All Rights Reserved