Polyram PlusTek RA300G7 Nylon 6.6 for Injection Molding, 35% Glass Fiber Reinforced, Heat Stabilized
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Glass Fiber Filled |
| Manufacturer | Polyram |
| Trade Name | PlusTek |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram PlusTek RA300G7 Nylon 6.6 for Injection Molding, 35% Glass Fiber Reinforced, Heat Stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Heat stabilized, 35% glass fiber reinforced Nylon 6.6 for injection molding applications.Information provided by Polyram.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 1.6 % | 1.6 % | 50% RH; ISO 62 |
| Water Absorption at Saturation | 5.0 % | 5.0 % | ISO 62 |
| Linear Mold Shrinkage | 0.0035 cm/cm | 0.0035 in/in | ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 122 | 122 | |
| Tensile Strength, Yield | 140 MPa | 20300 psi | ISO 527 |
| Elongation at Break | 2.5 % | 2.5 % | ISO 527 |
| Tensile Modulus | 7.00 GPa | 1020 ksi | ISO 527 |
| Flexural Strength | 250 MPa | 36300 psi | ISO 178 |
| Flexural Modulus | 8.50 GPa | 1230 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 8.50 kJ/m² | 4.04 ft-lb/in² | ISO 180 |
| Charpy Impact Unnotched | 4.00 J/cm² | 19.0 ft-lb/in² | ISO 179 |
| Charpy Impact, Notched | 0.650 J/cm² | 3.09 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 260 °C | 500 °F | ISO 11357 |
| Maximum Service Temperature, Air | 120 °C | 248 °F | Continuous use |
| 240 °C | 464 °F | Short peaks operation | |
| Deflection Temperature at 0.46 MPa (66 psi) | 265 °C | 509 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 255 °C | 491 °F | ISO 75 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 |
| Dielectric Constant | 3.5 @Frequency 1.00e+6 Hz |
3.5 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dielectric Strength | 90.0 kV/mm | 2290 kV/in | IEC 60250 |
Users viewing this material also viewed the following:
- Polymax® Maxelast® C4915 TPE, Transparent
- Pearl Engineering PEPLPET F097HA Film Grade Resin
- Asahi Kasei Tenac® 5012 Acetal Homopolymer (discontinued **)
- ICO Polymers ICORENEâ„¢ 110-1329 LMDPE Rotational Molding Resin
- Sinotek Materials ZSLZ89 Middle Carbon Graphite
- ELASTO UK Dryflex® 8006-101 Flame Retardant TPE for Extrusion, Natural, Halogen Free
- 3M AC-350 Class A-1/2 Aerospace Sealant
- Chem Polymer Chemlon 256 Nylon 6, Wire Jacketing Grade
- PolyOne Edgetek® NI-30GF/000 Nylon 6/10 - 30% Glass Fiber Reinforced (discontinued **)
- BASF 2-Butyne-1,4-diol Pure Cryst.
Copyright © lookpolymers.com All Rights Reserved