BASF Ultrason S 6010 PSU

Category Polymer , Thermoplastic , Polysulfone (PSU)
Manufacturer BASF
Trade Name Ultrason S
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultrason S 6010 PSU.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ultrason S 6010 is an unreinforced, high molecular weight injection-molding and extrusion grade with excellent chemical resistance (stress crack resistance) and good solubility in typical solvents (N-Methylpyrrolidone, Dimethylacetamide, Dichlormethane) used e.g. in the production of membranes or coatings, with reduced oligomer content. It conforms to FDA requirements of 21 CFR 177.1655.
Physical Properties Metric English Comments
Density 1.24 g/cc
0.0448 lb/in³
ISO 1183
Water Absorption 0.80 %
0.80 %
ISO 62
Moisture Absorption at Equilibrium 0.30 %
0.30 %
23°C/50% R.H.; ISO 62
Viscosity Test 81 cm³/g
81 cm³/g
Viscosity number
Linear Mold Shrinkage, Flow 0.0072 cm/cm
0.0072 in/in
ISO 294
Linear Mold Shrinkage, Transverse 0.0077 cm/cm
0.0077 in/in
ISO 294
Melt Flow 30 g/10 min

@Load 10.0 kg,
Temperature 360 °C
30 g/10 min

@Load 22.0 lb,
Temperature 680 °F
ISO 1133
Mechanical Properties Metric English Comments
Ball Indentation Hardness 135 MPa
19600 psi
ISO 2039-1
Tensile Strength at Break 75.0 MPa
10900 psi
5mm/min; ISO 527
Tensile Strength, Yield 75.0 MPa
10900 psi
50mm/min; ISO 527
Elongation at Break 5.7 %
5.7 %
5mm/min; ISO 527
Elongation at Yield 5.7 %
5.7 %
50mm/min; ISO 527
Tensile Modulus 2.60 GPa
377 ksi
ISO 527
Secant Modulus 0.0250 GPa

@Temperature 200 °C
3.63 ksi

@Temperature 392 °F
ISO 6721
0.800 GPa

@Temperature 175 °C
116 ksi

@Temperature 347 °F
ISO 6721
0.900 GPa

@Temperature 100 °C
131 ksi

@Temperature 212 °F
ISO 6721
0.950 GPa

@Temperature 50.0 °C
138 ksi

@Temperature 122 °F
ISO 6721
Izod Impact, Notched (ISO) 6.00 kJ/m²
2.86 ft-lb/in²
ISO 180/A
6.00 kJ/m²

@Temperature -30.0 °C
2.86 ft-lb/in²

@Temperature -22.0 °F
ISO 180/A
Charpy Impact Unnotched NB
NB
ISO 179/1eU
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
ISO 179/1eU
Charpy Impact, Notched 0.600 J/cm²
2.86 ft-lb/in²
ISO 179/1eA
0.600 J/cm²

@Temperature -30.0 °C
2.86 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
Tensile Creep Modulus, 1000 hours 2500 MPa
363000 psi
Elongation <0.5%, 23°C; ISO 899-1
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 53.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
29.4 µin/in-°F

@Temperature 73.4 - 176 °F
60.0 µm/m-°C

@Temperature 140 - 180 °C
33.3 µin/in-°F

@Temperature 284 - 356 °F
Maximum Service Temperature, Air 180 °C
356 °F
short cycle operations
Deflection Temperature at 1.8 MPa (264 psi) 175 °C
347 °F
ISO 75-2
Glass Transition Temp, Tg 187 °C
369 °F
10 K/min; ISO 11357-1/-3
Optical Properties Metric English Comments
Transmission, Visible 87 %

@Thickness 2.00 mm
87 %

@Thickness 0.0787 in
ASTM D 1003
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+13 ohm-cm
>= 1.00e+13 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+14 ohm
>= 1.00e+14 ohm
IEC 60093
Dielectric Strength 37.0 kV/mm
940 kV/in
IEC 60243-1 3
Comparative Tracking Index 125 V
125 V
Test Liquid A; IEC 60112
Processing Properties Metric English Comments
Melt Temperature 330 - 390 °C
626 - 734 °F
Mold Temperature 120 - 160 °C
248 - 320 °F
Descriptive Properties Value Comments
Color Natural
Commercial Status North America and Europe
FDA 21 CFR 177.1655
Impact Modified No
NSF Std. 61 Yes
Primary Processing Technique Injection Molding and Extrusion