Overview of materials for Thermoplastic Elastomer, Melt-Processible Rubber

Category	Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Elastomer, Melt-Processible Rubber
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Overview of materials for Thermoplastic Elastomer, Melt-Processible Rubber.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

This property data is a summary of similar materials in the MatWeb database for the category "Thermoplastic Elastomer, Melt-Processible Rubber". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.

Physical Properties	Metric	English	Comments
Density	0.180 - 1.99 g/cc	0.00650 - 0.0717 lb/in³	Average value: 1.03 g/cc Grade Count:671
Water Absorption	0.300 - 0.700 %	0.300 - 0.700 %	Average value: 0.488 % Grade Count:8
Oxygen Transmission	53.0 - 64.0 cc-mm/m²-24hr-atm	135 - 163 cc-mil/100 in²-24hr-atm	Average value: 58.0 cc-mm/m²-24hr-atm Grade Count:6
Viscosity	3250 - 720000 cP	3250 - 720000 cP	Average value: 148000 cP Grade Count:5
	17.0 - 5800 cP @Temperature 30.0 - 30.0 °C	17.0 - 5800 cP @Temperature 86.0 - 86.0 °F	Average value: 1.53e+6 cP Grade Count:21
	4000 - 5.00e+7 cP @Temperature 190 - 210 °C	4000 - 5.00e+7 cP @Temperature 374 - 410 °F	Average value: 1.53e+6 cP Grade Count:111
	4000 - 5.00e+7 cP @Shear Rate 0.100 - 11000 1/s	4000 - 5.00e+7 cP @Shear Rate 0.100 - 11000 1/s	Average value: 1.53e+6 cP Grade Count:111
Mooney Viscosity	5.80 - 48.0	5.80 - 48.0	Average value: 21.0 Grade Count:20
Linear Mold Shrinkage	0.000400 - 0.0420 cm/cm	0.000400 - 0.0420 in/in	Average value: 0.0148 cm/cm Grade Count:262
Linear Mold Shrinkage, Transverse	0.00300 - 0.0392 cm/cm	0.00300 - 0.0392 in/in	Average value: 0.0133 cm/cm Grade Count:37
Melt Flow	0.0800 - 150 g/10 min	0.0800 - 150 g/10 min	Average value: 11.3 g/10 min Grade Count:448

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	2.00 - 98.0	2.00 - 98.0	Average value: 63.4 Grade Count:623
	71.0 - 97.0 @Temperature 100 - 100 °C	71.0 - 97.0 @Temperature 212 - 212 °F	Average value: 84.8 Grade Count:10
	71.0 - 97.0 @Time 252000 - 3.60e+6 sec	71.0 - 97.0 @Time 70.0 - 1000 hour	Average value: 84.8 Grade Count:10
Hardness, Shore D	16.0 - 80.0	16.0 - 80.0	Average value: 45.6 Grade Count:89
Hardness, Shore OO	30.0 - 50.0	30.0 - 50.0	Average value: 40.0 Grade Count:3
Tensile Strength, Ultimate	0.255 - 51.0 MPa	37.0 - 7400 psi	Average value: 9.26 MPa Grade Count:573
	2.96475 - 43.5749 MPa @Temperature -40.0 - 85.0 °C	430.001 - 6320.01 psi @Temperature -40.0 - 185 °F	Average value: 23.0 MPa Grade Count:1
	10.9006 - 29.9646 MPa @Temperature 100 - 100 °C	1581.00 - 4346.01 psi @Temperature 212 - 212 °F	Average value: 23.0 MPa Grade Count:11
	10.9006 - 29.9646 MPa @Time 252000 - 3.60e+6 sec	1581.00 - 4346.01 psi @Time 70.0 - 1000 hour	Average value: 23.0 MPa Grade Count:11
Tensile Strength, Yield	0.0827 - 47.0 MPa	12.0 - 6820 psi	Average value: 4.49 MPa Grade Count:499
Film Elongation at Break, MD	740 - 1270 %	740 - 1270 %	Average value: 1060 % Grade Count:7
Film Elongation at Break, TD	820 - 1200 %	820 - 1200 %	Average value: 1070 % Grade Count:7
Elongation at Break	9.50 - 1660 %	9.50 - 1660 %	Average value: 582 % Grade Count:674
	780 - 1360 % @Temperature -40.0 - 85.0 °C	780 - 1360 % @Temperature -40.0 - 185 °F	Average value: 310 % Grade Count:1
	161.4 - 452 % @Temperature 100 - 100 °C	161.4 - 452 % @Temperature 212 - 212 °F	Average value: 310 % Grade Count:11
	161.4 - 452 % @Time 252000 - 3.60e+6 sec	161.4 - 452 % @Time 70.0 - 1000 hour	Average value: 310 % Grade Count:11
Elongation at Yield	16.0 - 100 %	16.0 - 100 %	Average value: 43.3 % Grade Count:9
	10.0 - 10.0 % @Temperature -35.0 - -35.0 °C	10.0 - 10.0 % @Temperature -31.0 - -31.0 °F	Average value: 10.0 % Grade Count:2
Modulus of Elasticity	0.000300 - 2.76 GPa	0.0435 - 400 ksi	Average value: 0.256 GPa Grade Count:64
Flexural Yield Strength	2.40 - 294 MPa	348 - 42700 psi	Average value: 48.2 MPa Grade Count:28
Flexural Modulus	0.00207 - 2.26 GPa	0.300 - 327 ksi	Average value: 0.274 GPa Grade Count:120
	0.0379212 - 2.07946 GPa @Temperature -40.0 - 85.0 °C	5.50009 - 301.605 ksi @Temperature -40.0 - 185 °F	Average value: 0.660 GPa Grade Count:2
Compressive Yield Strength	0.0900 - 2.33 MPa	13.1 - 338 psi	Average value: 0.661 MPa Grade Count:10
Compressive Modulus	0.00220 - 0.00760 GPa	0.319 - 1.10 ksi	Average value: 0.00416 GPa Grade Count:10
Resilience	5.00 - 67.0	5.00 - 67.0	Average value: 35.5 Grade Count:21
Rebound	12.0 - 40.0 %	12.0 - 40.0 %	Average value: 21.3 % Grade Count:4
Shear Modulus	0.00119 - 0.0115 GPa	0.173 - 1.67 ksi	Average value: 0.00466 GPa Grade Count:16
Secant Modulus	0.00336 - 0.110 GPa	0.487 - 16.0 ksi	Average value: 0.0242 GPa Grade Count:52
Izod Impact, Notched	0.267 J/cm - NB	0.500 ft-lb/in - NB	Average value: 2.43 J/cm Grade Count:23
	0.300 J/cm - NB @Temperature -40.0 - -20.0 °C	0.562 ft-lb/in - NB @Temperature -40.0 - -4.00 °F	Average value: 2.20 J/cm Grade Count:21
Gardner Impact	18.1 - 28.2 J	13.3 - 20.8 ft-lb	Average value: 23.0 J Grade Count:4
	12.5074 - 137.051 J @Temperature -30.0 - -6.67 °C	9.22501 - 101.083 ft-lb @Temperature -22.0 - 20.0 °F	Average value: 37.9 J Grade Count:17
Tear Strength Test	17.5 - 570	17.5 - 570	Average value: 284 Grade Count:11
Tear Strength	1.60 - 275 kN/m	9.13 - 1570 pli	Average value: 34.8 kN/m Grade Count:448
Peel Strength	0.470 - 1.35 kN/m	2.68 - 7.72 pli	Average value: 0.886 kN/m Grade Count:4
Graves Tear Strength	16.0 - 62.2 kN/m	91.3 - 355 pli	Average value: 32.8 kN/m Grade Count:45
	9.00 - 10.2 kN/m @Temperature 100 - 100 °C	51.4 - 58.2 pli @Temperature 212 - 212 °F	Average value: 9.58 kN/m Grade Count:6
Taber Abrasion, mg/1000 Cycles	0.00130 - 581	0.00130 - 581	Average value: 92.3 Grade Count:66
Compression Set	3.90 - 85.0 %	3.90 - 85.0 %	Average value: 27.7 % Grade Count:270
	22.0 - 100 % @Temperature 70.0 - 100 °C	22.0 - 100 % @Temperature 158 - 212 °F	Average value: 49.8 % Grade Count:94
	4.00 - 69.0 % @Temperature 70.0 - 125 °C	4.00 - 69.0 % @Temperature 158 - 257 °F	Average value: 49.8 % Grade Count:12
	4.00 - 69.0 % @Time 79200 - 1.21e+6 sec	4.00 - 69.0 % @Time 22.0 - 336 hour	Average value: 49.8 % Grade Count:12
Tensile Set	3.80 - 185 %	3.80 - 185 %	Average value: 24.8 % Grade Count:102
Film Tensile Strength at Break, MD	23.5 - 38.2 MPa	3410 - 5540 psi	Average value: 35.2 MPa Grade Count:7
Film Tensile Strength at Break, TD	24.5 - 38.2 MPa	3550 - 5540 psi	Average value: 31.0 MPa Grade Count:7
Torsional Stiffness	1.38 - 127 MPa	200 - 18500 psi	Average value: 14.2 MPa Grade Count:20

Electrical Properties	Metric	English	Comments
Electrical Resistivity	5.30e+15 - 3.00e+16 ohm-cm	5.30e+15 - 3.00e+16 ohm-cm	Average value: 2.18e+16 ohm-cm Grade Count:3
Dielectric Constant	2.30 - 2.51	2.30 - 2.51	Average value: 2.36 Grade Count:10