Polymer Resources AC-GP3 Acetal Copolymer, High Flow, Thin Walled Molding (Unverified Data**)

Category	Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Polymer Resources AC-GP3 Acetal Copolymer, High Flow, Thin Walled Molding (Unverified Data**).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation.

Physical Properties	Metric	English	Comments
Density	1.41 g/cc	0.0509 lb/in³	ASTM D792
Linear Mold Shrinkage	0.018 - 0.022 cm/cm	0.018 - 0.022 in/in	ASTM D955
Melt Flow	25 - 30 g/10 min	25 - 30 g/10 min	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	61.4 MPa	8900 psi	ASTM D638
Tensile Strength, Yield	61.4 MPa	8900 psi	ASTM D638
Flexural Strength	90.3 MPa	13100 psi	ASTM D790
Flexural Modulus	2.60 GPa	377 ksi	ASTM D790
Izod Impact, Notched	0.534 J/cm	1.00 ft-lb/in	ASTM D256
Gardner Impact	>= 22.6 J	>= 16.7 ft-lb	ASTM D3029

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	157 °C	315 °F	ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	110 °C	230 °F	ASTM D648
Flammability, UL94	HB	HB	1/16 in

Processing Properties	Metric	English
Rear Barrel Temperature	168 - 174 °C	335 - 345 °F
Middle Barrel Temperature	179 - 185 °C	355 - 365 °F
Front Barrel Temperature	185 - 191 °C	365 - 375 °F
Melt Temperature	182 - 199 °C	360 - 390 °F
Mold Temperature	76.7 - 93.3 °C	170 - 200 °F
Drying Temperature	79.4 - 85.0 °C	175 - 185 °F
Dry Time	3 - 4 hour	3 - 4 hour