Polyram PlusTek RA116 Nylon 6.6, Injection Molding
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced |
| Manufacturer | Polyram |
| Trade Name | PlusTek |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram PlusTek RA116 Nylon 6.6, Injection Molding.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | DIN 53479 |
| Water Absorption | 8.5 % | 8.5 % | DIN 53495 |
| Moisture Absorption at Equilibrium | 2.8 % | 2.8 % | 50%RH; DIN 53714 |
| Linear Mold Shrinkage | 0.014 - 0.018 cm/cm | 0.014 - 0.018 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 118 | 118 | ASTM-D785 |
| Tensile Strength, Yield | 85.0 MPa | 12300 psi | ASTM-D638 |
| Elongation at Break | 25 % | 25 % | ASTM-D638 |
| Tensile Modulus | 3.00 GPa | 435 ksi | ASTM-D790 |
| Flexural Strength | 135 MPa | 19600 psi | ASTM D790 |
| Flexural Modulus | 2.90 GPa | 421 ksi | ASTM-D790 |
| Izod Impact, Notched | 0.450 J/cm @Temperature 23.0 °C |
0.843 ft-lb/in @Temperature 73.4 °F |
ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 256 °C | 493 °F | |
| Maximum Service Temperature, Air | 70.0 °C | 158 °F | Continuous Use |
| 180 °C | 356 °F | Short peaks operation | |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | DIN 53461 |
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | DIN 53461 |
| Glow Wire Test | 750 °C | 1380 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | DIN 53482 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | DIN 53482 |
| Dielectric Constant | 3.6 @Frequency 1e+6 Hz |
3.6 @Frequency 1e+6 Hz |
VDE 0303/4 |
| Dielectric Strength | 120 kV/mm | 3050 kV/in | VDE 0303/4 |
Users viewing this material also viewed the following:
- PolyOne Trilliant™ HC X HC5200-0026 RS Natural Polypropylene, Unspecified (PP, Unspecified)
- NanoScale FAST-ACT® Formulation RNP-212
- ExxonMobil Escorene® LD-141 EVA Shrink Film Resin, FMI (discontinued **)
- Michelman® Licomer® W 19 Anionic / Nonionic polyethylene emulsion
- Universal Wire Works ER218 Stainless Steel Bare Wire
- 3M Scotch-Weld™ LSB90 Flexible Epoxy
- Arkema Group Rilsan® AMN G8 TLD Nylon 12, Graphite Filled (Dry)
- Braskem CP 202XP HECO Polypropylene Heterophasic Copolymer
- ATI Allegheny Ludlum Martensitic Stainless Steel Type 420, Hardened + 538°C Temper
- Austin Novel Materials Texalan® 685A Polyester and Polyether based TPU
Copyright © lookpolymers.com All Rights Reserved