A. Schulman POLYFORT™ FPP 1182E Talc Filled, Extrusion Grade Copolymer Polypropylene

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Talc Filler
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF A. Schulman POLYFORT™ FPP 1182E Talc Filled, Extrusion Grade Copolymer Polypropylene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
DescriptionPolyfort® FPP 1182E is a 20% talc-filled, extrusion grade copolymer polypropylene. It had a good balance of flexural modulus, low temperature impact, and appearance properties. Information provided by A. Schulman.
Physical Properties Metric English Comments
Specific Gravity 1.04 g/cc
1.04 g/cc
ASTM D792
Melt Flow 0.90 g/10 min

@Temperature 230 °C
0.90 g/10 min

@Temperature 446 °F
Condition L; ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 90
90
ASTM D785
Tensile Strength at Break 18.0 MPa
2610 psi
ISO 527
Tensile Strength, Yield 27.6 MPa
4000 psi
2 in/min; ASTM D638
Elongation at Yield 30 %
30 %
ASTM D638
Flexural Modulus 1.45 GPa
210 ksi
ASTM D790
Izod Impact, Notched 3.20 J/cm
6.00 ft-lb/in
ASTM D256
Izod Impact, Unnotched NB
NB
-22°F; ASTM D256
Gardner Impact 14.47 J
10.67 ft-lb
ASTM D3029
43.4 J

@Temperature -28.9 °C
32.0 ft-lb

@Temperature -20.0 °F
ASTM D3029
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 113 °C
235 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 50.0 °C
122 °F
ISO 75
62.8 °C
145 °F
ASTM D648
Descriptive Properties Value Comments
Thermal Oxidative Stability Pass
ASTM D3012, at 336 hrs, 150°C