Polyram PlusTek PB340S50 Nylon 6 for Injection Molding, 50% Glass-beads Reinforced, Heat Stabilized
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass Bead Filled |
| Manufacturer | Polyram |
| Trade Name | PlusTek |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram PlusTek PB340S50 Nylon 6 for Injection Molding, 50% Glass-beads Reinforced, Heat Stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
50% Glass-beads reinforced, heat stabilized Nylon 6 for injection molding applications.Information provided by Polyram.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.45 g/cc | 0.0524 lb/in³ | ISO 1183 |
| Water Absorption at Saturation | 5.8 % | 5.8 % | ISO 62 |
| Linear Mold Shrinkage | 0.0080 - 0.012 cm/cm | 0.0080 - 0.012 in/in | ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | ISO 527 |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527 |
| Tensile Modulus | 2.00 GPa | 290 ksi | ISO 527 |
| Flexural Strength | 120 MPa | 17400 psi | ISO 178 |
| Flexural Modulus | 3.00 GPa | 435 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 4.50 kJ/m² @Temperature 23.0 °C |
2.14 ft-lb/in² @Temperature 73.4 °F |
ISO 180 |
| 42.0 kJ/m² @Temperature -30.0 °C |
20.0 ft-lb/in² @Temperature -22.0 °F |
ISO 180 | |
| Charpy Impact Unnotched | 4.00 J/cm² @Temperature -30.0 °C |
19.0 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| 4.60 J/cm² @Temperature 23.0 °C |
21.9 ft-lb/in² @Temperature 73.4 °F |
ISO 179 | |
| Charpy Impact, Notched | 0.420 J/cm² @Temperature -30.0 °C |
2.00 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| 0.430 J/cm² @Temperature 23.0 °C |
2.05 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 218 °C | 424 °F | ISO 11357 |
| Maximum Service Temperature, Air | 80.0 °C | 176 °F | Continuous use |
| 180 °C | 356 °F | Short peaks operation | |
| Deflection Temperature at 0.46 MPa (66 psi) | 190 °C | 374 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C | 194 °F | ISO 75 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Dielectric Strength | 80.0 kV/mm | 2030 kV/in | IEC 60250 |
Users viewing this material also viewed the following:
- Polykemi AB POLYshine PBT D211 GF10 PBT, Glass Fiber Reinforced
- ExxonMobil OPTEMA™ TC 130 Molding, extrusion and compounding resin (discontinued **)
- Kennametal Stellite Deloro® 55 Nickel Alloy
- A. Schulman SCHULAMID® 66 GF13 13% Glass Fiber Reinforced Nylon 66
- DSM Arnitel® PL380 Polyether Ester Elastomer (European and Asian Grade)
- Asahi Kasei Tenac® 5050 Homopolymer Acetal Resin
- 3M Scotchcal™ 8000-37 Graphic Film
- DuPont Performance Polymers Minlon® 73M30 NC010 Nylon 6 (Unverified Data**)
- Lubrizol ESTANE® 58211 Ether Based Thermoplastic Polyurethane
Copyright © lookpolymers.com All Rights Reserved