| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Extruded |
| Manufacturer | Ineos ABS |
| Trade Name | Lustran® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos ABS Lustran® 552 Extrusion, Profile/Substrate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Properties tested in transverse direction (worst case) on 125-mil (3.2 mm) extruded sheets specimens with
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ASTM D792 |
| Melt Flow | 5.7 g/10 min @Load 10.0 kg, Temperature 230 °C |
5.7 g/10 min @Load 22.0 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 111 | 111 | ASTM D785 |
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | ASTM D638 |
| Tensile Modulus | 1.70 GPa | 247 ksi | ASTM D638 |
| Flexural Yield Strength | 59.3 MPa | 8600 psi | ASTM D790 |
| Flexural Modulus | 1.90 GPa | 276 ksi | ASTM D790 |
| Izod Impact, Notched | 2.10 J/cm @Thickness 3.17 mm |
3.93 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| 0.750 J/cm @Thickness 3.17 mm, Temperature -40.0 °C |
1.41 ft-lb/in @Thickness 0.125 in, Temperature -40.0 °F |
ASTM D256 | |
| Impact Test | 31.0 J @Thickness 2.50 mm |
22.9 ft-lb @Thickness 0.0984 in |
Instrumented Impact, Total Energy; 2.5 mm thick, 7.6 mph, 3 in. clamp, 0.5 in. dart; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C | 194 °F | |
| UL RTI, Electrical | 60.0 °C @Thickness 1.60 mm |
140 °F @Thickness 0.0630 in |
UL746B |
| UL RTI, Mechanical with Impact | 60.0 °C @Thickness 1.60 mm |
140 °F @Thickness 0.0630 in |
UL746B |
| UL RTI, Mechanical without Impact | 60.0 °C @Thickness 1.60 mm |
140 °F @Thickness 0.0630 in |
UL746B |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
Natural color |
| HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
Natural color |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 0.00 % | 0.00 % | Opaque only |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 6 GF 60 000/1M PA6 reinforced with 60% glass fibre
- Proto3000 Objet TangoGray FullCure950 Rubber-like Prototyping Polymer
- Solvay Specialty Polymers Halar® 500 ECTFE Fluoropolymer (discontinued **)
- Kureha KF Polymer 850 PVDF Homopolymer
- Heatbath/Park AL-2 Quenching and Tempering Salt
- Taiwan PU Corporation CPU-69-A/B Mixing Ratio 100/32 Polyurethane Casting Elastomer
- Styrolution Novodur® M210TF ABS
- Teknor Apex Telcar® TL-2560A Thermoplastic Elastomer
- Dow Corning 2-8197 EMULSION
Copyright © lookpolymers.com All Rights Reserved