Polyram PlusTek PA810 Nylon 6.6, Impact Modified
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Impact Grade |
| Manufacturer | Polyram |
| Trade Name | PlusTek |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram PlusTek PA810 Nylon 6.6, Impact Modified.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Impact modified polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | DIN 53479 |
| Water Absorption | 8.0 % | 8.0 % | DIN 53495 |
| Moisture Absorption at Equilibrium | 2.4 % | 2.4 % | 50%RH; DIN 53714 |
| Linear Mold Shrinkage | 0.014 - 0.018 cm/cm | 0.014 - 0.018 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 118 | 118 | ASTM-D785 |
| Tensile Strength, Yield | 70.0 MPa | 10200 psi | ASTM-D638 |
| Elongation at Break | 30 % | 30 % | ASTM-D638 |
| Flexural Strength | 90.0 MPa | 13100 psi | ASTM D790 |
| Flexural Modulus | 2.00 GPa | 290 ksi | ASTM-D790 |
| Izod Impact, Notched | 1.00 J/cm @Temperature 23.0 °C |
1.87 ft-lb/in @Temperature 73.4 °F |
ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 256 °C | 493 °F | |
| Maximum Service Temperature, Air | 80.0 °C | 176 °F | Continuous Use |
| 180 °C | 356 °F | Short peaks operation | |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | DIN 53461 |
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | DIN 53461 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | DIN 53482 |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | DIN 53482 |
| Dielectric Constant | 3.3 @Frequency 1e+6 Hz |
3.3 @Frequency 1e+6 Hz |
VDE 0303/4 |
| Dielectric Strength | 120 kV/mm | 3050 kV/in | VDE 0303/4 |
Users viewing this material also viewed the following:
- ND Industries 732 Gasket Maker Flexible
- Pacific Sintered Materials FX-233-T(HT) Infiltrated Alloy Steel
- Haynes 214® alloy sheet
- SABIC Innovative Plastics LNP STAT-KON OEL36A PPS - BRANCHED
- ExxonMobil Spartan EP 150
- EMS-Grivory Grivory® HT1V-5 HY black 9205 PA6T/6I-GF50
- Arlon UltraPad™ 51073G031D Silicone-Based Press Pad
- 3M Scotch-Weld™ EC-1469 Epoxy Adhesive
- DuPont Performance Polymers Delrin® 588P NC010 Acetal Homopolymer (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved