3M Dyneon™ TR 1105 PTFE  (discontinued **)

Category Polymer , Thermoplastic , Fluoropolymer , PTFE
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF 3M Dyneon™ TR 1105 PTFE  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ideal for thin wall ram extrusion productsReduces cold flow and melt viscosityLower permeabilityLower porosityWeldableExcellent product smoothnessIncreased machine outputInformation provided by Dyneon, A 3M Company
Physical Properties Metric English Comments
Bulk Density 0.820 g/cc
0.0296 lb/in³
ASTM D4894
Density 2.16 g/cc
0.0780 lb/in³
ASTM D4894
Particle Size 800 µm
800 µm
average; ASTM D4894
Deformation 2.0 %

@Pressure 15.00 MPa
2.0 %

@Pressure 2175 psi
ASTM D621
4.0 %

@Time 86400 sec,
Pressure 15.00 MPa
4.0 %

@Time 24.0 hour,
Pressure 2175 psi
ASTM D621
Mechanical Properties Metric English Comments
Hardness, Shore D 62
62
Initial; ASTM D2240
58

@Time 15.0 sec
58

@Time 0.00417 hour
ASTM D2240
Tensile Strength at Break 27.6 MPa
4000 psi
ASTM D4894
Elongation at Break 400 %
400 %
ASTM D4894
Tensile Modulus 0.6498 GPa
94.25 ksi
ASTM D638
Thermal Properties Metric English Comments
CTE, linear 112 µm/m-°C

@Temperature 30.0 - 100 °C
62.0 µin/in-°F

@Temperature 86.0 - 212 °F
ASTM E831
146 µm/m-°C

@Temperature 100 - 200 °C
81.0 µin/in-°F

@Temperature 212 - 392 °F
ASTM E831
178 µm/m-°C

@Temperature 200 - 300 °C
99.0 µin/in-°F

@Temperature 392 - 572 °F
ASTM E831
Thermal Conductivity 0.230 W/m-K

@Temperature 100 °C
1.60 BTU-in/hr-ft²-°F

@Temperature 212 °F
ASTM E1530
0.240 W/m-K

@Temperature 250 °C
1.67 BTU-in/hr-ft²-°F

@Temperature 482 °F
ASTM E1530
Shrinkage 5.5 %
5.5 %
ASTM D4994
Electrical Properties Metric English Comments
Dielectric Strength 3.70 kV/mm
94.0 kV/in
ASTM D149
Descriptive Properties Value Comments
Powder Flow Properties Very good