Total PPC 2660 Polypropylene, Heterophasic Copolymer

Category Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer Total Atofina
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Total PPC 2660 Polypropylene, Heterophasic Copolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
ATOFINA Polypropylene PPC 2660 is a heterophasic copolymer. PPC 2660 is characterized by a low fluidity hence good melt strength to provide ease of processing and good manufactured article properties.ApplicationPPC 2660 is suitable for the extrusion of corrugated cardboard, blown film, sheet and pipes and for blow-molding applications where a very high impact resistance is required. Information provided provided by Total Petrochemicals.Total Petrochemicals acquired former Fina and Atofina plastics product lines.
Physical Properties Metric English Comments
Bulk Density 0.525 g/cc
0.0190 lb/in³
ISO 1183
Density 0.905 g/cc
0.0327 lb/in³
ISO 1183
Melt Flow 0.80 g/10 min

@Load 2.16 kg,
Temperature 230 °C
0.80 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell R 74
74
ISO 2039-2
Tensile Strength, Yield 24.0 MPa
3480 psi
ISO 527-2
Elongation at Yield 13 %
13 %
ISO 527-2
Tensile Modulus 1.20 GPa
174 ksi
ISO 527-2
Flexural Modulus 1.10 GPa
160 ksi
ISO 527-2
Izod Impact, Notched (ISO) 50.0 kJ/m²
23.8 ft-lb/in²
ISO 179
6.00 kJ/m²

@Temperature -20.0 °C
2.86 ft-lb/in²

@Temperature -4.00 °F
ISO 179
Charpy Impact, Notched >= 5.00 J/cm²
>= 23.8 ft-lb/in²
0.600 J/cm²

@Temperature -20.0 °C
2.86 ft-lb/in²

@Temperature -4.00 °F
ISO 179
Thermal Properties Metric English Comments
Melting Point 165 °C
329 °F
ISO 3146
Deflection Temperature at 0.46 MPa (66 psi) 90.0 °C
194 °F
120°C per hour; ISO 75-2
Deflection Temperature at 1.8 MPa (264 psi) 48.0 °C
118 °F
120°C per hour; ISO 75-2
Vicat Softening Point 60.0 °C
140 °F
50N-50°C per hour; ISO 306
130 °C
266 °F
10N-50°C per hour; ISO 306