Polymer Resources PPX-FR7 Modified PPO, V-0 Flame Retardant, Medium Heat, 250 HDT (Unverified Data**)

Category	Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, Heat Resistant
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Polymer Resources PPX-FR7 Modified PPO, V-0 Flame Retardant, Medium Heat, 250 HDT (Unverified Data**).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation.

Physical Properties	Metric	English	Comments
Density	1.10 g/cc	0.0397 lb/in³	ASTM D792
Linear Mold Shrinkage	0.0050 - 0.0070 cm/cm	0.0050 - 0.0070 in/in	ASTM D955
Melt Flow	4.0 - 8.0 g/10 min	4.0 - 8.0 g/10 min	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	55.2 MPa	8000 psi	ASTM D638
Tensile Strength, Yield	62.1 MPa	9000 psi	ASTM D638
Flexural Strength	110 MPa	16000 psi	ASTM D790
Flexural Modulus	2.62 GPa	380 ksi	ASTM D790
Izod Impact, Notched	1.60 J/cm	3.00 ft-lb/in	ASTM D256
Gardner Impact	>= 22.6 J	>= 16.7 ft-lb	ASTM D3029

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	127 °C	260 °F	ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	121 °C	250 °F	ASTM D648
Flammability, UL94	V-0	V-0	1/8 in

Processing Properties	Metric	English
Rear Barrel Temperature	249 - 299 °C	480 - 570 °F
Middle Barrel Temperature	260 - 304 °C	500 - 580 °F
Front Barrel Temperature	271 - 310 °C	520 - 590 °F
Melt Temperature	288 - 316 °C	550 - 600 °F
Mold Temperature	71.1 - 98.9 °C	160 - 210 °F
Drying Temperature	104 - 110 °C	220 - 230 °F
Dry Time	3 - 4 hour	3 - 4 hour

Users viewing this material also viewed the following: