- Polymer Property : Melt Flow = 8.0 g/10 min
Polymer Property : Melt Flow = 8.0 g/10 min Product List
Physical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 1.0 - 8.0 g/10 min @Load 2.16 kg, Temperature 265 °C |
1.0 - 8.0 g/10 min @Load 4.76 lb, Temperature 509 °F |
ASTM D1238 |
| Polymer Resources PC/TP-GP3-G20 PC/Polyester Alloy, 20% Glass Reinforced Superior Chemical Resistance, 20% Glass ReinforcedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information pr.. |
|||
| Melt Flow | 4.0 - 8.0 g/10 min | 4.0 - 8.0 g/10 min | ASTM D1238 |
| Polymer Resources PPX-FR3-[color]EN Modified PPO, UL 94 V-1 with HDT of 265 F, Extrusion Grade Process: ExtrusionNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation. |
|||
| Melt Flow | 4.0 - 8.0 g/10 min @Load 11.6 kg, Temperature 250 °C |
4.0 - 8.0 g/10 min @Load 25.6 lb, Temperature 482 °F |
ASTM D1238 |
| Polymer Resources PPX-FR7 Modified-PPO, V-0 Flame Retardant Modified-Polyphenylene Oxide, V-0 Flame Retardant, 260F HDTProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Infor.. |
|||
| Melt Flow | 4.0 - 8.0 g/10 min @Load 2.16 kg, Temperature 210 °C |
4.0 - 8.0 g/10 min @Load 4.76 lb, Temperature 410 °F |
ASTM D1238 |
| NatureWorks® Ingeo™ 6400D Fiber Grade PLA NatureWorks® PLA polymer 6400D is a thermoplastic fiber-grade resin derived primarily from annually renewable resources. Available in pellet form, 6400D is designed for extrusion into mechanically .. |
|||
| Melt Flow | 6.0 - 8.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
6.0 - 8.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238-00 |
| Ipiranga Petrochem PCC 0742 Polypropylene The production of polypropylene (PP) employs Spheripol technology from Montell / Italy. This technology has been acclaimed all over the world and is known as clean technology, because it does not pr.. |
|||
| Melt Flow | 4.0 - 8.0 g/10 min @Load 5.00 kg, Temperature 230 °C |
4.0 - 8.0 g/10 min @Load 11.0 lb, Temperature 446 °F |
ASTM D1238 |
| Kureha KF Polymer 2950 PVDF Copolymer KF Polymer is a fire-resistant engineering plastic which maintains the excellent performance of a fluoropolymer. It shows well-balanced molding processability similar to general-purpose resins. KF p.. |
|||
| Melt Flow | 4.0 - 8.0 g/10 min @Load 5.00 kg, Temperature 230 °C |
4.0 - 8.0 g/10 min @Load 11.0 lb, Temperature 446 °F |
ASTM D1238 |
| Solvay Specialty Polymers Solef® 11010 Polyvinylidene Fluoride (PVDF) Solef® 11010 PVDF is a medium-viscosity flexible PVDF copolymer resin and is typically processed by extrusion.Features: Copolymer; Good Flexibility; Medium ViscosityAdditional Properties: Crystal.. |
|||
| Melt Flow | 4.0 - 8.0 g/10 min @Load 5.00 kg, Temperature 230 °C |
4.0 - 8.0 g/10 min @Load 11.0 lb, Temperature 446 °F |
ASTM D1238 |
| Solvay Specialty Polymers Solef® 6010 Polyvinylidene Fluoride (PVDF) Solef® 6010 PVDF homopolymer has medium viscosity and is typically processed by extrusion.Features: Homopolymer; Medium ViscosityAdditional Properties: Crystallization Heat - ASTM D3417 54.0 to 6.. |
|||
| Melt Flow | 4.0 - 8.0 g/10 min @Load 12.5 kg, Temperature 230 °C |
4.0 - 8.0 g/10 min @Load 27.6 lb, Temperature 446 °F |
ISO 1133 |
| Shanghai Ofluorine 9201F PVDF Powder for cables Description: Excellent mechanical properties, heat resistance and flame resistance, PVDF for cable can bear high temperature, corrosive chemicals etc harsh working environment, which has low smoke, .. |
|||
| Melt Flow | 4.0 - 8.0 g/10 min | 4.0 - 8.0 g/10 min | ASTM D1238 |
| A. Schulman POLYFLAM™ RCP 770C/CW DescriptionPolyflam® RCP 770C/CW is a flame-retardant concentrate based in low-density polyethylene that features excellent dispersion and processing stability up to 550°F.ApplicationRCP 770 C/CW.. |
|||
| Melt Flow | 4.0 - 8.0 g/10 min | 4.0 - 8.0 g/10 min | ASTM D1238 |
| A. Schulman POLYFLAM™ RCP 505C Flame Retardant Concentrate Based In Low-Density Polyethylene Information provided by A. Schulman. |
|||
| Melt Flow | 6.0 - 8.0 g/10 min @Temperature 230 °C |
6.0 - 8.0 g/10 min @Temperature 446 °F |
ASTM D1238 |
| A. Schulman POLYFORT™ 1602 UV-3120 UV Stabilized, Glass Reinforced Copolymer Polypropylene DescriptionPolyfort® FPP 1602 UV-3120 is a black UV stabilized 10% chemically coupled glass reinforced copolymer polypropylene.Information provided by A. Schulman. |
|||
| Melt Flow | 4.0 - 8.0 g/10 min | 4.0 - 8.0 g/10 min | ASTM D1238 |
| A. Schulman POLYFLAM™ RCP 505C Flame Retardant Concentrate Based In Low-Density Polyethylene Information provided by A. Schulman. |
|||
| Melt Flow | 4.0 - 8.0 g/10 min | 4.0 - 8.0 g/10 min | ASTM D1238 |
| A. Schulman POLYFLAM™ RCP 500 C DescriptionPolyflam® RCP 500C is an economical flame-retardant concentrate based in low-density polyethylene that features excellent dispersion and processing stability up to 550°F. ApplicationRC.. |
|||
| Melt Flow | 4.0 - 8.0 g/10 min | 4.0 - 8.0 g/10 min | ASTM D1238 |
| A. Schulman POLYFLAM™ RCP 770C/CW DescriptionPolyflam® RCP 770C/CW is a flame-retardant concentrate based in low-density polyethylene that features excellent dispersion and processing stability up to 550°F.ApplicationRCP 770 C/CW.. |
|||
| Melt Flow | 6.0 - 8.0 g/10 min @Temperature 230 °C |
6.0 - 8.0 g/10 min @Temperature 446 °F |
ASTM D1238 |
| A. Schulman POLYFORT™ 1602 UV-3120 UV Stabilized, Glass Reinforced Copolymer Polypropylene DescriptionPolyfort® FPP 1602 UV-3120 is a black UV stabilized 10% chemically coupled glass reinforced copolymer polypropylene.Information provided by A. Schulman. |
|||
| Melt Flow | 6.0 - 8.0 g/10 min @Temperature 230 °C |
6.0 - 8.0 g/10 min @Temperature 446 °F |
ASTM D1238 |
| A. Schulman POLYFORT™ 1602 UV-3120 UV Stabilized, Glass Reinforced Copolymer Polypropylene DescriptionPolyfort® FPP 1602 UV-3120 is a black UV stabilized 10% chemically coupled glass reinforced copolymer polypropylene.Information provided by A. Schulman. |
|||
| Melt Flow | 4.0 - 8.0 g/10 min | 4.0 - 8.0 g/10 min | ASTM D1238 |
| A. Schulman POLYFLAM™ RCP 770C/CW DescriptionPolyflam® RCP 770C/CW is a flame-retardant concentrate based in low-density polyethylene that features excellent dispersion and processing stability up to 550°F.ApplicationRCP 770 C/CW.. |
|||
| Melt Flow | 6.0 - 8.0 g/10 min @Temperature 230 °C |
6.0 - 8.0 g/10 min @Temperature 446 °F |
ASTM D1238 |
| A. Schulman POLYFORT™ 1602 UV-3120 UV Stabilized, Glass Reinforced Copolymer Polypropylene DescriptionPolyfort® FPP 1602 UV-3120 is a black UV stabilized 10% chemically coupled glass reinforced copolymer polypropylene.Information provided by A. Schulman. |
|||
| Melt Flow | 6.0 - 8.0 g/10 min | 6.0 - 8.0 g/10 min | ISO 1133 |
| Chengdu Polyster H605 Thermoplastic Polyether-ester Elastomer (TPEE) Medium modulus molding and injection grade. Contains improved color- stable antioxidants. Excellent tear resistance. Molded and injected products for consumer use, such as airbag door covers, railwa.. |
|||
| Melt Flow | 4.0 - 8.0 g/10 min @Load 5.00 kg, Temperature 235 °C |
4.0 - 8.0 g/10 min @Load 11.0 lb, Temperature 455 °F |
|
| Daikin NEOFLON EA-LR43 ETFE Pellets Due to its excellent melt flow properties, NEOFLON ETFE can be processed in the same was as other thermoplastic resins. NEOFLON ETFE is also highly suited to such secondary processes as welding, fl.. |
|||
| Melt Flow | 3.0 - 8.0 g/10 min | 3.0 - 8.0 g/10 min | |
| Daikin NEOFLON RP-4040 EFEP Pellets NEOFLON EFEP is an ETFE based fluoropolymer combining the excellent physical properties derived from ETFE together with a low processing temperature that is more compatible with conventional thermop.. |
|||
| Melt Flow | 6.0 - 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
6.0 - 8.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
|
| Breplast Bretene SPF M Thermoplastic Composite, 70% PP + 30% PE Recovered polypropylene and polyethylene compositeInformation provided by Breplast S.p.A. |
|||
| Melt Flow | 1.0 - 8.0 g/10 min | 1.0 - 8.0 g/10 min | ASTM D1238 |
| Buckeye Polymers BP RPPC 2008 C BLK Polypropylene, Calcium Filled Product Information: Calcium Carbonate Filled PP Grades have a high impact toughness, moderate increased stiffness, and excel in high gloss applications. Our BP RPP C series product line ranges fro.. |
|||
| Melt Flow | 3.0 - 8.0 g/10 min @Load 12.5 kg, Temperature 232 °C |
3.0 - 8.0 g/10 min @Load 27.6 lb, Temperature 450 °F |
ASTM D1238 |
| Arkema Group KYNAR FLEX® 2800-00 Polyvinylidene Fluoride Copolymer - Extrusion Characteristics: Natural resin - translucent, off-white hemispheres. Flexible. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mechanical strength, low.. |
|||
| Melt Flow | 3.0 - 8.0 g/10 min @Load 21.6 kg, Temperature 232 °C |
3.0 - 8.0 g/10 min @Load 47.6 lb, Temperature 450 °F |
ASTM D1238 |
| Arkema Group KYNAR® LBG1 Polyvinylidene Fluoride Powder Characteristics: White, non-hygroscopic powder.Applications: Membrane, Lithium ion battery applicationsInformation provided by Arkema Inc. |
|||
| Melt Flow | 4.0 - 8.0 g/10 min @Load 5.00 kg, Temperature 230 °C |
4.0 - 8.0 g/10 min @Load 11.0 lb, Temperature 446 °F |
ASTM D1238 |
| Solvay Specialty Polymers Solef® 11010 Polyvinylidene Fluoride (PVDF)
(Unverified Data**) Solef® 11010 PVDF is a medium-viscosity flexible PVDF copolymer resin and is typically processed by extrusion.Information provided by Solvay Specialty Polymers. |
|||
| Melt Flow | 4.0 - 8.0 g/10 min | 4.0 - 8.0 g/10 min | ASTM D1238 |
| Polymer Resources PPX-FR7 Modified PPO, V-0 Flame Retardant, Medium Heat, 250 HDT
(Unverified Data**) Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation. |
|||
| Melt Flow | 3.0 - 8.0 g/10 min @Load 12.5 kg, Temperature 232 °C |
3.0 - 8.0 g/10 min @Load 27.6 lb, Temperature 450 °F |
ASTM D1238 |
| Arkema Group KYNAR® 2801-00 Polyvinylidene Fluoride Powder Characteristics: White, non-hygroscopic powder. Flexible. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mechanical strength, low permeability, abrasi.. |
|||
| Melt Flow | 3.0 - 8.0 g/10 min @Load 5.00 kg, Temperature 190 °C |
3.0 - 8.0 g/10 min @Load 11.0 lb, Temperature 374 °F |
ISO 1133 |
| Polyplastic Armoflen® PO MF 75-2 Linear Low Density Polyethylene, 75% Calcium Carbonate Information provided by PolyPlastic Group. |
|||