Lehmann & Voss LUVOCOMÂ® 1106-8124 Polyether imide, lubricant modified

Category	Polymer , Thermoplastic , Polyetherimide (PEI)
Manufacturer	Lehmann & Voss & Co.
Trade Name	LUVOCOM®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Lehmann & Voss LUVOCOMÂ® 1106-8124 Polyether imide, lubricant modified.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Applications: High continuous use and heat distortion temperature. Non flammable.Dynamic stressed parts at high movement velocity.High dimensionally stable precision parts.Information provided by Lehmann & Voss & Co.KG

Physical Properties	Metric	English	Comments
Specific Gravity	1.35 g/cc	1.35 g/cc	ISO 1183
Water Absorption	<= 0.30 %	<= 0.30 %	23Â°C/24h
Linear Mold Shrinkage	0.0050 - 0.0080 cm/cm	0.0050 - 0.0080 in/in

Mechanical Properties	Metric	English	Comments
Tensile Stress	105 MPa	15200 psi
Elongation at Yield	4.8 %	4.8 %
	6.0 %	6.0 %	flexural
Modulus of Elasticity	4.00 GPa	580 ksi
Flexural Strength	150 MPa	21800 psi
Flexural Modulus	3.40 GPa	493 ksi
Charpy Impact Unnotched	5.00 J/cmÂ²	23.8 ft-lb/inÂ²	edgewise; ISO 179 1eU
Charpy Impact, Notched	0.600 J/cmÂ²	2.86 ft-lb/inÂ²	ISO 179 1eA

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	170 Â°C	338 Â°F

Electrical Properties	Metric	English	Comments
Insulation Resistance	>= 1.00e+12 ohm	>= 1.00e+12 ohm

Processing Properties	Metric	English	Comments
Processing Temperature	380 Â°C	716 Â°F	mass temp
Nozzle Temperature	350 - 400 Â°C	662 - 752 Â°F
Zone 1	330 - 350 Â°C	626 - 662 Â°F
Zone 2	340 - 390 Â°C	644 - 734 Â°F
Zone 3	350 - 400 Â°C	662 - 752 Â°F
Mold Temperature	150 - 180 Â°C	302 - 356 Â°F
Drying Temperature	120 Â°C @Time >=28800 sec	248 Â°F @Time >=8.00 hour	Dehumidifying dryer
	150 Â°C @Time >=14400 sec	302 Â°F @Time >=4.00 hour	or

Descriptive Properties	Value	Comments
Color	black