Polymer Resources PC/TP-GP2-G10 PC/Polyester Alloy, 10% Glass Reinforced
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/PET Polyester Blend, Glass Reinforced , Polyester, TP |
| Manufacturer | Polymer Resources, LTD |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polymer Resources PC/TP-GP2-G10 PC/Polyester Alloy, 10% Glass Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Excellent Chemical Resistance, 10% Glass ReinforcedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.30 g/cc | 1.30 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 - 0.0080 cm/cm | 0.0040 - 0.0080 in/in | ASTM D955 |
| Melt Flow | 2.0 - 10 g/10 min @Load 2.16 kg, Temperature 265 °C |
2.0 - 10 g/10 min @Load 4.76 lb, Temperature 509 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 65.5 MPa | 9500 psi | ASTM D638 |
| Tensile Strength, Yield | 65.5 MPa | 9500 psi | ASTM D638 |
| Flexural Strength | 128 MPa | 18500 psi | ASTM D790 |
| Flexural Modulus | 4.00 GPa | 580 ksi | ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm @Temperature 22.8 °C |
2.00 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 113 °C | 235 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 104 °C | 220 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0626 in |
|
| HB @Thickness 3.17 mm |
HB @Thickness 0.125 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 263 - 285 °C | 505 - 545 °F | |
| Middle Barrel Temperature | 268 - 291 °C | 515 - 555 °F | |
| Front Barrel Temperature | 274 - 296 °C | 525 - 565 °F | |
| Melt Temperature | 260 - 288 °C | 500 - 550 °F | |
| Mold Temperature | 65.6 - 87.8 °C | 150 - 190 °F | |
| Drying Temperature | 104 - 110 °C | 220 - 230 °F | |
| Dry Time | 4.00 - 6.00 hour | 4.00 - 6.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Vent | 0.0015 |
Users viewing this material also viewed the following:
- NanoAmor 90%, OD: 1-2 nm OH Functionalized Single-Walled Carbon Nanotubes
- Lubrizol Advanced Materials Pearlstick® 45-50/03 Linear Thermoplastic Polyurethane Elastomer (discontinued **
- KEP Kepital® F20 Acetal Copolymer
- Karina 801-18/489-C-IS Gray PVC Compound
- Total PPC 11812 S01 Polypropylene, Heterophasic Copolymer, Injection Molding
- Crucible Steel CRUCIBLE A9 Tool Steel
- Dow Nordel® IP 4570 EPDM Hydrocarbon Rubber
- Addiplast Addilene J 522 K20 Polypropylene Copolymer
- 3M Scotch-Weld™ 826 Nitrile Rubber & Plastic Adhesive
Copyright © lookpolymers.com All Rights Reserved