Teknor Apex Chemlon® 133 G Nylon 66, 33% Short Glass Fiber Filled
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled , Nylon 66, Glass Fiber Filled, Flame Retardant |
| Manufacturer | Teknor Apex Company |
| Trade Name | Chemlon® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Teknor Apex Chemlon® 133 G Nylon 66, 33% Short Glass Fiber Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Notes: Flammability: Passes, FMVSS 302 Processing Method: Injection Molding Forms: Pellets FMVSSInformation Provided by Teknor Apex
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.38 g/cc | 1.38 g/cc | ASTM D792 |
| Water Absorption | 0.90 % | 0.90 % | 24 hr; ASTM D750 |
| Linear Mold Shrinkage | 0.0015 - 0.0040 cm/cm | 0.0015 - 0.0040 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 176 MPa | 25500 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Elongation at Yield | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Strength | 276 MPa | 40000 psi | ASTM D790 |
| Flexural Modulus | 8.62 GPa | 1250 ksi | ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm @Temperature 22.8 °C |
2.00 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 50.4 µm/m-°C | 28.0 µin/in-°F | ASTM D696 |
| Melting Point | 257 °C | 495 °F | DSC |
| Deflection Temperature at 1.8 MPa (264 psi) | 249 °C | 480 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB @Thickness 0.7607 mm |
HB @Thickness 0.02995 in |
|
| Oxygen Index | 25 % | 25 % | ASTM D2863 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | ASTM D257 |
| Dielectric Strength | 16.1 kV/mm @Thickness 3.00 mm |
410 kV/in @Thickness 0.118 in |
ASTM D149 |
| Comparative Tracking Index | 600 V | 600 V | UL 746 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 246 - 257 °C | 475 - 495 °F | |
| Middle Barrel Temperature | 263 - 274 °C | 505 - 525 °F | |
| Front Barrel Temperature | 268 - 282 °C | 515 - 540 °F | |
| Nozzle Temperature | 268 - 282 °C | 515 - 540 °F | |
| Melt Temperature | 263 - 282 °C | 505 - 540 °F | Processing Temperature |
| Drying Temperature | 79.4 °C | 175 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Suggested Moisture, max | 0.2 | |
| Suggested Regrind, max | 25 |
Users viewing this material also viewed the following:
- ND Industries StudGrade® 146 Permanent StudGrade HD Threadlocker
- SABIC Innovative Plastics Lexan® 920A PC
- SABIC Innovative Plastics ULTEM CRS5001 PEI
- Shin-Etsu Silicones FE-361U Fluorosilicone Elastomer
- STAR Thermoplastic Alloys & Rubbers StarFlex® P 7335-1000 TPE
- Formosa Plastics Formolon® 622F PVC
- Ecomass® 1080ZD94 Tungsten Filled Polyamide
- Chevron Phillips Marlex® H516HP High Density Polyethylene, Pressure Pipe Grade
- CP-Polymer-Technik Wellamid® 6600/58 GV 30 HWCP 30% Glass Fiber Nylon 66, Impact Modified Until -40°C, Heat Stabilized, Conditioned
- LG Chemical SG175G ABS, Super Surface Gloss, High Flow
Copyright © lookpolymers.com All Rights Reserved