- Polymer Resources PCSF-FR G30 Polycarbonate, 30% Glass Reinforced Structural Foam Grade
Polymer Resources PCSF-FR G30 Polycarbonate, 30% Glass Reinforced Structural Foam Grade
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Foam Grade, Glass Filled |
| Manufacturer | Polymer Resources, LTD |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polymer Resources PCSF-FR G30 Polycarbonate, 30% Glass Reinforced Structural Foam Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Process: Foam MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Foam grades tested with foamed parts with a 10% weight reduction relative to unfoamed parts.Information provided by Polymer Resources Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0020 - 0.0050 cm/cm | 0.0020 - 0.0050 in/in | ASTM D955 |
| Melt Flow | 3.0 - 7.0 g/10 min | 3.0 - 7.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 68.9 MPa | 10000 psi | ASTM D638 |
| Tensile Strength, Yield | 68.9 MPa | 10000 psi | ASTM D638 |
| Flexural Strength | 125 MPa | 18200 psi | ASTM D790 |
| Flexural Modulus | 6.55 GPa | 950 ksi | ASTM D790 |
| Izod Impact, Unnotched | 5.34 J/cm | 10.0 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 138 °C | 280 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 132 °C | 270 °F | ASTM D648 |
| Flammability, UL94 | V-0 | V-0 | 1/8 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 254 - 266 °C | 490 - 510 °F | |
| Middle Barrel Temperature | 293 - 310 °C | 560 - 590 °F | |
| Front Barrel Temperature | 293 - 310 °C | 560 - 590 °F | |
| Melt Temperature | 288 - 316 °C | 550 - 600 °F | |
| Mold Temperature | 71.1 - 104 °C | 160 - 220 °F | |
| Drying Temperature | 118 - 124 °C | 245 - 255 °F | |
| Dry Time | 3 - 4 hour | 3 - 4 hour |
Users viewing this material also viewed the following:
- Polymer Resources NY6-G30 Nylon 6, 30% Glass Reinforced
- LATI Latamid SP1 G/30 PA 6.10, 30% Glass Fiber Reinforced
- Techmer ES HiFill® PA6 GF25 L BK 25% Glass Filled
- Shin-Etsu Silicones X-22-8278 Fluid
- Shinil Chemical SHINCON PMMA Electro Conductive Polymer
- Unitika E-RUNG60 Ultra high-rigidity PA6, Dry
- Hexcel® HexWeb® CR III 3/8-5052-.0025 Corrosion Resistant Specification Grade Aluminum Honeycomb
- Braskem FF018F Homopolymer Polypropylene
- Arkema Group Rilsan® MA 4411 Nylon 12, Flexible Tubing Grade (Conditioned)
- Kazanorgsintez P2ES-12 Electrically Conductive Polyethylene Composite
Copyright © lookpolymers.com All Rights Reserved