Polyram RamTal PM1013 Acetal, General Purpose
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced |
| Manufacturer | Polyram |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram RamTal PM1013 Acetal, General Purpose.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
General purpose polyacetal copolymer for injection molding applications.Information provided by Polyram Ram On Ind.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | DIN 53479 |
| Water Absorption | 0.22 % | 0.22 % | DIN 53495 |
| Linear Mold Shrinkage | 0.018 - 0.022 cm/cm | 0.018 - 0.022 in/in | |
| Melt Flow | 13 g/10 min @Load 2.16 kg, Temperature 190 °C |
13 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 82 | 82 | ASTM-D785 |
| Tensile Strength, Yield | 65.0 MPa | 9430 psi | ASTM-D638 |
| Elongation at Break | 25 % | 25 % | ASTM-D638 |
| Flexural Strength | 85.0 MPa | 12300 psi | ASTM-D790 |
| Flexural Modulus | 2.80 GPa | 406 ksi | ASTM-D790 |
| Izod Impact, Notched | 0.600 J/cm @Temperature 23.0 °C |
1.12 ft-lb/in @Temperature 73.4 °F |
ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 165 °C | 329 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | DIN 53461 |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | DIN 53461 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | DIN 53482 |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | DIN 53482 |
| Dielectric Constant | 3.8 @Frequency 1e+6 Hz |
3.8 @Frequency 1e+6 Hz |
VDE 0303/4 |
| Dielectric Strength | 24.0 kV/mm | 610 kV/in | VDE 0303/4 |
Users viewing this material also viewed the following:
- MV Labs SR400 SrCl2·6H2O Strontium chloride hexahydrate
- Radici Radilon® SRCP3010LK (dry) Nylon 6
- Lucite International Lucite® 4F Acrylic Bead Resin
- Solvay Specialty Polymers Torlon® 4601 Polyamide-imide (PAI)
- A. Schulman PAPERMATCH® H-5338 Specialty Masterbatch
- A. Schulman POLYBATCH™ Cedar 10310U Concentrate Based In LLDPE
- Tra-Con Tra-Cast FS330 Fire Retardant Long Pot Life Epoxy Casting Compound
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 20 PHR Carbon Black, N-550 (FEF)
- DuPont Performance Polymers Hypalon® 48 Chlorosulfonated Polyethylene Rubber, Gum Compound (discontinued **)&
Copyright © lookpolymers.com All Rights Reserved